A mullite/glass composite has been prepared by reactive sintering of a kaolinite clay/mica-rich kaolin waste mixture with 25 wt% waste. Phase composition, microstructure, dielectric and electrical properties of the composite fired at 1400 °C were evaluated by X-ray diffraction, scanning electron microscopy and impedance spectroscopy (between 25 and 600 °C in air). The microstructural characterization showed the attainment of dense samples composed of acicular (orthorhombic) mullite (47.6 wt%), glassy phase (50.1 wt%), and residual quartz (2.3 wt%). Electrical conductivity (1.9x10-8 S/cm at 300 °C), dielectric constant (6.7 at 1 MHz, 25 °C) and dielectric loss (0.024 at 1 MHz, 25 °C) results gave evidence that the mullite/glass composite is a promising low-cost material for commercial use in electronics-related applications.

Este estudo aborda os efeitos do processamento na microestrutura e nas propriedades de compósitos alumina-mulita via sinterização reativa de uma mistura argila caulinítica e hidróxido de alumínio. Amostras prensadas a 40 MPa foram sinterizadas entre 1300 e 1600 °C. As propriedades tecnológicas foram determinadas em função da temperatura de sinterização. A avaliação das fases cristalinas e da microestrutura foi realizada por difração de raios X e microscopia eletrônica. Os resultados indicaram a obtenção de mulita e alumina a partir de 1300 °C. Para sinterizações acima de 1450 °C foram obtidos valores de porosidade aparente inferiores a 0,8% e tensão de ruptura à flexão superior a 40 MPa. Amostras com morfologia bimodal (grãos equiaxiais e alongados) e resistência mecânica de 70 MPa foram obtidas após sinterização a 1600 °C. Este estudo demonstra a possibilidade de preparar compósitos alumina-mulita de baixo custo e com propriedades tecnológicas compatíveis com as de cerâmicas produzidas por companhias com grande atuação no mercado internacional de produtos refratários.