Nitrogen-doped graphene quantum dots (N-GQDs) are widely used in biosensing, catalysis, and energy storage due to their excellent conductivity, high specific surface area, unique quantum size effects, and optical properties. In this paper, we successfully synthesized N-GQDs using a facile hydrothermal approach and investigated the effects of different hydrothermal temperatures and times on the morphology and structure of N-GQDs. The results indicated that the size of N-GQDs gradually increased and they eventually aggregated into graphene fragments with increasing temperature or reaction time. Notably, N-GQDs synthesized at 180 °C for 6 h exhibited the most uniform size, with an average diameter of approximately 3.48 nm, a height of 5–6 graphene layers, as well as favorable fluorescence properties. Moreover, the surface of N-GQDs contained abundant oxygen- and nitrogen-containing functional groups, which could provide numerous active sites for electrode reactions. The assembled electrode exhibited typical pseudocapacitive behavior with exceptional electrochemical performance, achieving a specific capacitance of 102 F g⁻¹ at a current density of 1 A g⁻¹. In a 10,000-cycle test, the electrode demonstrated excellent cycling stability with a capacitance retention rate of 78.5%, which laid the foundation for practical application of the electrode. This work successfully applied N-GQDs in supercapacitors, offering new insights into their development for the energy storage field.

Based on MnO₂/carbon cloth (CC) composite materials, an Ag-doped MnO₂ nanowire, self-assembled, urchin-like structure was synthesized in situ on the surface of CC using a simple method, and a novel and efficient flexible electrode material for supercapacitors was developed. The morphology, structure, elemental distribution, and pore distribution of the material were analyzed using SEM, TEM, XRD, XPS, and BET. The electrochemical performance was tested using cyclic voltammetry (CV) and galvanostatic charge/discharge (GCD). In the three-electrode system, GCD testing showed that the specific capacitance of the material reached 520.8 F/g at 0.5 A/g. After 2000 cycles at a current density of 1 A/g, the capacitance retention rate was 90.6%, demonstrating its enormous potential in the application of supercapacitor electrode materials.

This study investigated the effect of different monomer compositions of acrylonitrile (AN) and methyl methacrylate (MMA) on the synthesis and expansion performance of thermally expandable microspheres (TEMs). TEMs with different monomer ratios, specifically AN to MMA ratios of 100:0, 90:10, 80:20, and 70:30, were synthesized via free radical suspension polymerization. The inner morphology, crystallinity, blowing agent encapsulation efficiency, and expansion ratio of the microspheres were analyzed using scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and other characterization techniques. The results showed that as the MMA content and reaction time increased, the internal structure of the microsphere shell became more uniform, and its thickness increased. Notably, the P(AN:MMA)(90:10) microspheres exhibited the lowest expansion temperature and the highest expansion ratio. This study provides a theoretical basis for the further optimization of TEM synthesis processes.