Polyethylene granules of diameter 2 mm were treated with a low-pressure weakly ionized air plasma created in a metallic chamber by a pulsed microwave discharge of pulse duration 180 μs and duty cycle 70%. Optical emission spectroscopy showed rich bands of neutral nitrogen molecules and weak O-atom transitions, but the emission from N atoms was below the detection limit. The density of O atoms in the plasma above the samples was measured with a cobalt catalytic probe and exhibited a broad peak at the pressure of 80 Pa, where it was about 2.3 × 10²¹ m⁻³. The samples were characterized by X-ray photoelectron spectroscopy. Survey spectra showed oxygen on the surface, while the nitrogen concentration remained below the detection limit for all conditions. The high-resolution C1s peaks revealed formation of various functional groups rather independently from treatment parameters. The results were explained by extensive dissociation of oxygen molecules in the gaseous plasma and negligible flux of N atoms on the polymer surface.

This research focused on enhancement of mechanical properties in carbon fiber (CF)-filler-reinforced linear low-density polyethylene (PE) matrix composites. A hand layup method using an oven was used as the fabrication method. Improvement in adhesion was achieved by oxygen plasma treatment to the PE matrix. CF and PE were initially mixed by normal stirring, ultrasonication and mechanical stirring before being filtered and dried for fabrication. Better tensile results were observed with a plasma-treated polyethylene (PEP)/10 wt.% CF combination, with a maximum tensile strength of 21.5 MPa and improvement in the properties of up to 12.57% compared to non-plasma PE with the same CF addition. The addition of carbon fibers at 13 and 15 wt.% resulted in a reduction in the tensile strength properties to 18.2 MPa and 17.7 MPa, respectively. This reduction in tensile strength was due to agglomeration of CF with plasma- and non-plasma-treated PE. The fabrication condition of 180 °C temperature for 20 min showed better tensile properties than other conditions. The SEM results following tensile testing revealed enhanced CF filler adherence with plasma PE results, as well as fewer surface deformations. A higher flexural strength of 25.87 MPa was observed for the plasma treated PE/7 wt.% CF combination.

Polyethylene powder of average particle diameter of 160 µm was activated in a plasma reactor made from aluminum of volume 64 dm³ at the pressure 100 Pa. Dense oxygen plasma was sustained with a microwave discharge powered by a pulsed magnetron source of power 1 kW mounted onto the top flange of the plasma reactor. Polymer powder was treated in a batch mode with 0.25 kg/batch. The powder was placed into a stainless-steel dish mounted in the center of the reactor where diffusing plasma of low ion density, and the O-atom density of 2 × 10²¹ m⁻³ was sustained. The powder was stirred in the dish at the rate of 40 rpm. The evolution of powder wettability versus treatment time was measured using the Washburne method, and the surface composition was determined by X-ray Photoelectron Spectroscopy (XPS). The wettability versus the oxygen concentration assumed a parabolic behavior. The maximal oxygen concentration, as revealed by XPS, was 17.5 at.%, and the maximal increase of wettability was 220%. The efficiency of O-atoms utilization in these experimental conditions was about 10% taking into account the spherical geometry of dust particles and perfectly smooth surface. The method is scalable to large industrial systems.

The paper describes an experimental investigation of the possibility of industrial modification of surface wettability and adhesion of polymers by the action of a plasma of a gliding discharge generated in air at atmospheric pressure in a simulated production process. The test material was polypropylene plates (PP). The modification was performed by a device with a multi-electrode (four pairs) system, which is not common. The quality of pre-processing and usability was evaluated primarily in terms of the industrial requirements, which means a change in wettability and adhesion expressed by the contact angle/surface free energy value in dependence to sample exposure time expressed by the conveyor belt speed. The surface free energy assessment of a treated polymeric surface by contact angle measurement was carried out by analyzing static sessile drops and evaluated by Owens–Wendt–Rabel–Kaelble (OWRK) model. The results determined a set of operating parameters at which the modification process meets the industrial requirements. By evaluating the change in surface free energy in relation to the storage time, the degree of hydrophobic recovery of the treated samples, i.e. the time stability of the plasma-treated surface, was also determined. It has been found that plasma-treated PP surface fully meets industrial demands and can be stored for at least 50 days.

Plasma treatment of polyethylene powder was carried out in low-pressure gaseous plasma sustained in a semi-industrial reactor powered with a microwave source, in which it was specifically worked with the residual atmosphere. Timed applications of plasma-treated powder in air atmosphere were carried out to study their influence on the adhesion. Based on wettability and adhesion, a treatment time of 5 min was selected for the study of other working gases (nitrogen, oxygen, hydrogen, argon and a mixture of nitrogen and hydrogen). The measurements of wettability showed the highest adhesion increase for nitrogen. The highest increase of adhesion and of surface oxygen contain shown by oxygen treatment. By contrast, treatment with hydrogen resulted in increased roughness of the sintered surface of the powder. The selection of appropriate working gases which are not standard in industrial processes enables one to atypically regulate the adhesion or wettability.