The limited access to fresh water and the increased presence of emergent pollutants (EPs) in wastewater has increased the interest in developing strategies for wastewater remediation, including photocatalysis. Graphitic carbon nitride (g-C₃N₄) is a 2D non-metal material with outstanding properties, such as a 2.7 eV bandgap and physicochemical stability, making it a promising photocatalyst. This work reports the process of obtaining high-surface-area (SA) g-C₃N₄ using the thermal-exfoliation process and the posterior effect of Ag-nanoparticle loading over the exfoliated g-C₃N₄ surface. The photocatalytic activity of samples was evaluated through methylene blue (MB) degradation under visible-light radiation and correlated to its physical properties obtained by XRD, TEM, BET, and UV–Vis analyses. Moreover, 74% MB degradation was achieved by exfoliated g-C₃N₄ compared to its bulk counterpart (55%) in 180 min. Moreover, better photocatalytic performances (94% MB remotion) were registered at low Ag loading, with 5 wt.% as the optimal value. Such an improvement is attributed to the synergetic effect produced by a higher SA and the role of Ag nanoparticles in preventing charge-recombination processes. Based on the results, this work provides a simple and efficient methodology to obtain Ag/g-C₃N₄ photocatalysts with enhanced photocatalytic performance that is adequate for water remediation under sunlight conditions.

This study reports the synthesis, characterization, and catalytic performance of a series of catalysts of Ru supported on CeO₂-Y₂O₃ composites (Ru/CeYX; X = 0, 33, 66, and 100 wt.% Y₂O₃) for CO₂ hydrogenation. Supported material modification (Y₂O₃-CeO₂), by the Y₂O₃ incorporation, allowed a change in selectivity from methane to RWGS of the CO₂ hydrogenation reaction. This change in selectivity is correlated with the variation in the physicochemical properties caused by Y₂O₃ addition. X-ray diffraction (XRD) analysis confirmed the formation of crystalline fluorite-phase CeO₂ and α-Y₂O₃. High-resolution transmission electron microscopy (HR-TEM) and energy-dispersive X-ray spectroscopy (EDS) elemental mapping revealed the formation of a homogeneous CeO₂-Y₂O₃ nanocomposite. As the Y₂O₃ content increased, the specific surface area, measured by BET, showed a decreasing trend from 106.3 to 51.7 m² g⁻¹. X-ray photoelectron spectroscopy (XPS) of Ce3d indicated a similar Ce³⁺/Ce⁴⁺ ratio across all CeO₂-containing materials, while the O1s spectra showed a reduction in oxygen vacancies with increasing Y₂O₃ content, which is attributed to the decreased surface area upon composite formation. Catalytically, the addition of Y₂O₃ influenced both conversion and selectivity. CO₂ conversion decreased with increasing Y₂O₃ content, with the lowest conversion observed for Ru/CeY100. Regarding selectivity, methane was the dominant product for Ru/CeY0 (pure CeO₂), while CO was the main product for Ru/CeY33, Ru/CeY66, and Ru/CeY100, indicating a shift towards the reverse water–gas shift (RWGS) reaction. The highest RWGS reaction rate was observed with the Ru/CeY33 catalyst under all tested conditions. The observed differences in conversion and selectivity are attributed to a reduction in active sites due to the decrease in surface area and oxygen vacancies, both of which are important for CO₂ adsorption. In order to verify the surface species catalytically active for RWGS, the samples were characterized by FTIR spectroscopy under reaction conditions.