Whether plastic packaging waste is disposed of in different bins (source separation, S) or in a single bin (post source separation, P) is generally assumed to impact the waste stream's quality. To elucidate this question, we evaluated the quality of LDPE, HDPE, and PP plastic waste from both separation systems (S and P) through a concise analytical strategy. The materials received similar treatment after collection (e.g., washing, NIR-sorting). A multivariate approach to ATR-FTIR spectroscopy was developed to assess their material composition and the effect of washing. Results were complemented by TGA, DSC, and py-GC/MS analysis. The material performance was investigated by a lab-scale extrusion and granulation, followed by an assessment of the mechanical properties and the melt volume rate. Our study reveals the HDPE materials to be of good quality, regardless of their source. For LDPE and PP, the P-materials are fractionally more contaminated after washing. Both PP-materials display poor material performance with highly fluctuating elongations-at-break (between 30% and 380%). S-LDPE was found to contain more polymeric impurities than P-LDPE. We conclude that the quality depends strongly on the material type and on the treatment after collection (washing, sorting). The multivariate approach to FTIR data evaluation we propose aims at simplifying the quality evaluation of polyolefin waste plastics and may serve as a basis for future work in this field.

This study provides insight into the causes of inferior long-term stability of nanocomposites based on organic layered silicates (OLSs) used for cable mantles. A hierarchy was established by analyzing bentonite products and their respective polyolefin nanocomposites. Thermogravimetric analysis (TGA), X-ray diffraction (XRD), gas adsorption, energy-dispersive spectroscopy (SEM-EDX), and infrared spectroscopy (IR) provided evidence for the adsorption of stabilizers onto the filler surface and thus their reduction in activity, promoting polymer oxidation. This behavior corresponds to the specific surface area of the incorporated OLS. Therefore, it can be stated that gas adsorption and XRD are especially useful for the evaluation of long-term photostability. It was revealed that photocatalytically active iron is of secondary importance since iron-rich bentonites still formed the most stable nanocomposite. This also applies to the Hofmann elimination products of the modifying agent, where higher contents do not accelerate the degradation process. No elimination products could be traced within the composites. Due to the polymer-filler interface being essential for long-term photostability, prior analysis of the filler surface properties can be used to estimate the stability of the respective nanocomposite as a rationale for product selection in the early stages of development. The reasons identified in this work for decreasing the long-term photostability of OLS nanocomposites compared with unfilled formulations is an important step toward increasing their stability.

The commercialization of poly(butylene succinate-co-adipate) (PBSA), a biodegradable and potentially fully biobased random copolyester, is still ongoing. Due to its high relevance as mono material or as blend component in flexible film applications, a sound understanding of compounding, further processing and film properties is necessary. In this work, PBSA, poly (lactic acid) (PLA) and blends at three different compositions thereof were processed into flat films and blown films, respectively. Investigating the films with X-ray diffraction (XRD), multivariate confocal Raman microscopy (CRM) and scanning electron microscopy (SEM) revealed the semicrystalline order as well as the blend morphology. While PBSA is semicrystalline, PLA remains amorphous after the processing step. As imaged by CRM, flat films exhibit lamellar-like domains formed during uniaxial stretching and rapid cooling, whereas blown films show no pronounced preferential orientation. Tensile tests in both the machine and transverse directions demonstrate the versatility of PBSA and its blends in spanning a wide range of mechanical strength and flexibility, covering and partly exceeding the stiffness and strength ranges typically reported for commodity polyolefins while exhibiting reduced ductility. Differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA) provide further insights into the thermal properties of the pure and blend materials.