Composite material (AC-ZnO) was prepared by growing ZnO nanoparticles during the production of biomass based-activated carbon (AC) via the incorporation of zinc acetate in the process. Comprehensive analyzes confirmed the presence of ZnO nanoparticles over the AC surface and described the particular nature of the composite adsorbent. Methylene blue (MB) equilibrium data fitted the Dubinin Raduskevich model. The MB adsorption capacity was higher for the bare activated carbons (197.9–188.7 mg/g) than the activated carbons with ZnO nanoparticles (137.6–149.7 mg/g). The adsorption of the MB on the adsorbents is physical because the mean adsorption energy (E) is between 1.76 and 2.00 kJ/mol. Experiments that combine adsorption and photocatalytic process were carried out with different loads of adsorbents and with and without UV-light exposure. Photocatalytic activity was identified mostly in the first stage of the adsorption process and in the case of experiments with less load of the composite AC-ZnO, because the light obstruction effect of the activated carbon is more for higher loads. The ZnO grown over AC improves the adsorption of cations such as Pb, Al and Fe in aqueous phase (polluted river water) and provides antibacterial capacity against Escherichia coli and Salmonella typhimurium.

Microporous–mesoporous activated carbons from five different types of agro-industrial wastes were produced using chemical activation with ZnCl₂ and carbonization at mild conditions of 600 °C, comprehensively characterized and investigated for removal of methylene blue (MB) in aqueous solution, a model large-molecular-size organic pollutant. The external part of the mango pit (mango seed husk) was used for the production of activated carbon (AC) for the first time. Despite that the raw agro-materials exhibited significantly different porosity, all activated carbons produced possessed well-developed microporous–mesoporous structures showing high surface areas and micropore volumes. Further, it was revealed that the pore size distribution of raw agro-material is a more important property in development of microporous–mesoporous structure of produced ACs than their overall porosity. All activated carbons produced adsorbed MB, reaching in most cases 100 % removal from the aqueous phase. Adsorption data were fitted well to a pseudo-second-order kinetic model. For MB adsorption, the mesoporosity and the ratio of micropores accessible for MB were the key factors since there exists the size-selectivity effect on MB adsorption due to MB molecular dimensions. The molecular dimensions of MB were estimated via DFT calculations to 1.66 × 0.82 × 0.54 nm, and this parameter was correlated with determined micropore size distributions of activated carbons.