The dump temperature and mixing interval between rubber, silica, and silane coupling agent for silica-filled natural rubber (NR) tire tread compounds using bis-triethoxysilylpropyl tetrasulfide (TESPT) as silane were optimized. The dump temperature turns out to be the key parameter governing the properties of the silica-filled NR compounds. The increase in viscosity of the compounds by changing the dump temperature from 100 to 150 °C indicates that inevitably some cross-linking of NR occurs by sulfur contained in TESPT, simultaneous with the silanization reaction between silica and silane. However, the viscosity decreases again when dump temperatures above 150 °C are applied, indicating a dominant occurrence of degradation of the NR molecules. The results are in good agreement with bound rubber contents. The overall properties indicate that a dump temperature in the range of 135–150 °C and a silica–silane–rubber mixing interval of 10 min are the most appropriate mixing conditions for silica-filled NR compounds with TESPT as coupling agent.

Modern fuel-saving tire treads are commonly reinforced by silica due to the fact that this leads to lower rolling resistance and higher wet grip compared to carbon black-filled alternatives. The introduction of secondary fillers into the silica-reinforced tread compounds, often named hybrid fillers, may have the potential to improve tire performance further. In the present work, two secondary fillers organoclay nanofiller and N134 carbon black were added to silica-based natural rubber compounds at a proportion of silica/secondary filler of 45/10 phr. The compounds were prepared with variable mixing temperatures based on the mixing procedure commonly in use for silica-filled NR systems. The results of Mooney viscosity, Payne effect, cure behavior, and mechanical properties imply that the silica hydrophobation and coupling reaction of the silane coupling agent with silica and elastomer are significantly influenced by organoclay due to an effect of its modifier: an organic ammonium derivative. This has an effect on scorch safety and cure rate. The compounds where carbon black was added as a secondary filler do not show this behavior. They give inferior filler dispersion compared to the pure silica-filled compound, attributed to an inappropriate high mixing temperature and the high specific surface area of the carbon black used. The dynamic properties indicate that there is a potential to improve wet traction and rolling resistance of a tire tread when using organoclay as secondary filler, while the combination of carbon black in silica-filled NR does not change these properties.

Diphenyl guanidine (DPG) is an essential ingredient in silica-reinforced rubber compounds for low rolling resistance tires, as it not only acts as a secondary accelerator, but also as a catalyst for the silanization reaction. However, because of concern over the toxicity of DPG that liberates aniline during high-temperature processing, safe alternatives are required. The present work studies several amines as potential alternatives for DPG. Different amines (i.e., hexylamine, decylamine, octadecylamine, cyclohexylamine, dicyclohexylamine, and quinuclidine) are investigated in a model system, as well as in a practical rubber compound by taking the ones with DPG and without amine as references. The kinetics of the silanization reaction of the silica/silane mixtures are evaluated using model compounds. The mixtures with amines show up to 3.7 times higher rate constants of the primary silanization reaction compared to the compound without amine. Linear aliphatic amines promote the rate constant of the primary silanization reaction to a greater extent compared to amines with a cyclic structure. The amines with short-alkyl chains that provide better accessibility towards the silica surface, enhance the primary silanization reaction more than the ones with long-alkyl chains. The different amines have no significant influence on the rate constant of the secondary silanization reaction. The amine types that give a higher primary silanization reaction rate constant show a lower flocculation rate in the practical compounds. For the systems with a bit lower primary silanization reaction rate, but higher extent of shielding or physical adsorption that still promotes higher interfacial compatibility between the elastomer and the filler surface, the rubber compounds show a lower Payne effect which would indicate lower filler-filler interaction. However, the flocculation rate constant remained high.

This review article highlights and summarizes the recent developments in the field of surface modification methods for aramid fibers. Special focus is on methods that create a multifunctional fiber surface by incorporating nanostructures and enabling mechanical interlocking. To give a complete picture of adhesion promotion with aramids, the specific questions related to the challenges in aramid-matrix bonding are also shortly presented. The main discussion of the surface modification approaches is divided into sections according to how material is added to the fiber surface; (1) coating, (2) grafting and (3) growing. To provide a comprehensive view of the most recent developments in the field, other methods with similar outcomes, are also shortly reviewed. To conclude, future trends and insights are discussed.

The rubber formulation plays a significant role in the properties of NR compounds filled with silica. In this work, the influences of various silicas, silane coupling agents, and diphenylguanidine (DPG) on the properties of compounds and vulcanizates—that is, cure characteristics, Mooney viscosity, flocculation kinetics, bound rubber content, Payne effect, tan δ at 60°C, tensile properties, and tear properties—are investigated. The results demonstrate that compound viscosity and curing behavior, as well as vulcanizate properties of the silica-filled NR, are much improved by incorporating silane coupling agents. Bis-triethoxysilylpropyltetrasulfide clearly gives better overall properties than the disulfide-based silane bis-triethoxysilylpropyldisulfide, except for scorch safety. DPG acts as a synergist to sulfenamide primary accelerators, as well as activator for the silanization reaction. Highly dispersible (HD) silicas can significantly enhance the degree of dispersion and so lead to higher filler–rubber interaction. As a consequence, the HD silicas provide better dynamic and mechanical properties for filled NR vulcanizates compared with conventional counterparts. The optimal quantities of both silane coupling agent and DPG required in the formulation are correlated to the cetyl trimethylammonium bromide specific surface area of the silicas. Furthermore, the results reveal that the silica structure as characterized by the dibutylphthalate adsorption also strongly influences the reinforcing efficiency.