Emulsion electrospinning is a method of modifying a fibers’ surface and functional properties by encapsulation of the bioactive molecules. In our studies, bovine serum albumin (BSA) played the role of the modifier, and to protect the protein during the electrospinning process, the W/O (water-in-oil) emulsions were prepared, consisting of polymer and micelles formed from BSA and anionic (sodium dodecyl sulfate–S) or nonionic (Tween 80–T) surfactant. It was found that the micelle size distribution was strongly dependent on the nature and the amount of the surfactant, indicating that a higher concentration of the surfactant results in a higher tendency to form smaller micelles (4–9 µm for S and 8–13 µm for T). The appearance of anionic surfactant micelles reduced the diameter of the fiber (100–700 nm) and the wettability of the nonwoven surface (up to 77°) compared to un-modified PCL polymer fibers (100–900 nm and 130°). The use of a non-ionic surfactant resulted in better loading efficiency of micelles with albumin (about 90%), lower wettability of the nonwoven fabric (about 25°) and the formation of larger fibers (100–1100 nm). X-ray photoelectron spectroscopy (XPS) was used to detect the presence of the protein, and UV-Vis spectrophotometry was used to determine the loading efficiency and the nature of the release. The results showed that the location of the micelles influenced the release profiles of the protein, and the materials modified with micelles with the nonionic surfactant showed no burst release. The release kinetics was characteristic of the zero-order release model compared to anionic surfactants. The selected surfactant concentrations did not adversely affect the biological properties of fibrous substrates, such as high viability and low cytotoxicity of RAW macrophages 264.7.

For several decades, there has been growing interest in the influence of low-frequency magnetic fields (LFMFs) and red LED light on the healing process. Keratinocytes are cells that play a significant role in the process of wound healing and tissue regeneration. A human keratinocyte cell line (HaCaT) was exposed to an LFMF with low induction (180–195 Hz; 60 µT, magnetostimulation), red LED light (630 nm; 300 mW, LED therapy), and their combined action (magneto-LED therapy) in in vitro culture conditions. On day 4 and 8 of the experiment, the following parameters were determined: adhesion/proliferation, adenylate kinase (AK), nitric oxide (NO), cytokines (IL-1β, IL-6, IL-8, IL-10, IL-12p70, TNF-α), metalloproteinases (MMP-2, MMP-9), and collagen IV. It was shown that magnetostimulation caused an increase in keratinocyte adhesion/proliferation and IL-8 secretion and a decrease in IL-12 secretion. The LED therapy resulted in a transient increase in the secretion of NO and cytokines IL-1, IL-12, and IL-6 in keratinocytes. The use of magneto-LED therapy resulted in an increase in keratinocyte adhesion/proliferation, the secretion of cytokines IL-6 and IL-8, and NO with a simultaneous decrease in MMP-9 secretion. The results of our studies showed that the action of an LFMF with low-induction and LED light on keratinocytes can modulate the biological activity of keratinocytes towards improving the skin healing process.

Background: Ankle fractures are among the most common injuries requiring surgical intervention. Standard radiographs are typically used for postoperative assessment; however, some patients continue to experience residual symptoms despite satisfactory radiographic outcomes. Weight-bearing computed tomography (WBCT), though not yet widely integrated into clinical practice, offers potential advantages in evaluating lower-limb deformities, injuries, and arthritis. This study explores the utility of WBCT for the midterm assessment following ankle fracture fixation and compares its findings with those obtained from standard radiographs. Methods: In this retrospective case study, we analyzed the correlations between the functional outcome scores approximately one year post-surgery and parameters assessed using WBCT. Pearson’s correlation coefficient was used to evaluate these correlations, and a t-test was performed to assess their statistical significance, with a threshold p-value of 0.05. Additionally, Spearman’s rank correlation coefficient was calculated as a supplementary descriptive measure, without significance testing. These correlations were then compared with those obtained from standard ankle radiographic views (anteroposterior, lateral, and mortise). Results: Several correlations were identified between WBCT parameters and functional scales, with certain parameters demonstrating high statistical significance (p < 0.05). Overall, the correlations observed for WBCT were stronger than those for standard radiographs. Conclusions: Although the study cohort was limited, the findings suggest that WBCT may provide additional insights beyond conventional radiography. Further research with larger patient groups is needed to establish its clinical relevance.