The closed-cell micro-pore magnesium composite foam with hollow ceramic microspheres (CMs) was fabricated by a modified melt foaming method. The effect of CMs on the compressive deformation behavior of CM-containing magnesium composite foam was investigated. Optical microscopy and scanning electron microscopy were used for observation of the microstructure. Finite element modeling of the magnesium composite foam was established to predict localized stress, fracture of CMs, and the compressive deformation behavior of the foam. The results showed that CMs and pores directly affected the compressive deformation behavior of the magnesium composite foam by sharing a part of load applied on the foam. Meanwhile, the presence of Mg₂Si phase influenced the mechanical properties of the foam by acting as the crack source during the compression process.

Magnesium composite foams with 10 vol. % of hollow ceramic microspheres (CMs) were prepared by modified melt foaming method. Specimens with homogeneous pore structures were subjected to various heating temperature (150, 250, 320, 400, and 500 °C, respectively) and enduring times (1, 2, 4, 6, and 24 h, respectively). Evolution of microstructure and mechanical properties of the samples, before and after the heating processes were examined by applying X-ray diffraction technique (XRD), differential scanning calorimetry (DSC), scanning electron microscopy (SEM), and quasi-static uniaxial compression test. The results showed that as heating temperature and enduring time increasing, β-Mg₁₇Al₁₂ phases gradually dissolved, resulting in a solid-solution strengthening effect. Meanwhile, internal stress relaxation in the matrix leads to the decrease of yield strength and micro hardness of the specimens. When compared with the unheated foams, the treated specimens possessed lower micro-hardness, yield strength, and energy absorption capacity due to the dissolution of β-Mg₁₇Al₁₂ phases and the release of internal stress. However, higher strain hardening exponents for almost all of the treated composite foams were observed and the reasons were discussed. It is proposed that more factors should be taken into account when using heated composite foams in practical applications.