Alginate and algal-biomass (Laminaria digitata) beads were prepared by homogeneous Ca ionotropic gelation. In addition, glutaraldehyde-crosslinked poly (ethyleneimine) (PEI) was incorporated into algal beads. The three sorbents were characterized by scanning electron microscopy (SEM) coupled with energy dispersive X-ray analysis (EDX): the sorption occurs in the whole mass of the sorbents. Sorption experiments were conducted to evaluate the impact of pH, sorption isotherms, and uptake kinetics. A special attention was paid to the effect of drying (air-drying vs. freeze-drying) on the mass transfer properties. For alginate, freeze drying is required for maintaining the porosity of the hydrogel, while for algal-based sorbents the swelling of the material minimizes the impact of the drying procedure. The maximum sorption capacities observed from experiments were 415, 296 and 218 mg Pb g⁻¹ and 112, 77 and 67 mg Cu g⁻¹ for alginate, algal and algal/PEI beads respectively. Though the sorption capacities of algal-beads decreased slightly (compared to alginate beads), the greener and cheaper one-pot synthesis of algal beads makes this sorbent more competitive for environmental applications. PEI in algal beads decreases the sorption properties in the case of the sorption of metal cations under selected experimental conditions.

Two kinds of algal beads were prepared using a carrageenan-based alga (Chrondrus crispus) and an alginate-based alga (Laminara digitata) ionotropically gelled with K(I) and Ca(II), respectively: the process consists of biopolymer partial extraction followed by hydrogel formation. The beads were modified with branched polyethylenimine (bPEI) and glutaraldehyde (GA) using the impregnation method to improve their sorption capacity for Pd(II) in acid solution. SEM-EDX and FTIR techniques were used for characterizing the beads. The impacts of pH and presence of anions, cations, and Pt(IV) were studied in batch experiments. The beads were also applied for Pd(II) recovery from synthesized leaching liquors of a spent catalyst and a car catalytic converter via the sorption-desorption process. Results show that Pd is concentrated in the outer layer of L. digitata-bPEI-GA composite (LD/PEI) beads, while in the case of the C. crispus-bPEI-GA composite (CC/PEI), it is homogenously distributed in the whole mass of the sorbents. The difference is attributed to the repulsive force of the outer Ca(II)-alginate barrier of LD/PEI beads that makes it difficult for the branched polymer PEI to penetrate through the layer and be immobilized in the inner compartment. As a result, LD/PEI beads possess a lower maximum sorption capacity, but a slightly faster uptake at pH 1 than CC/PEI beads. In addition, CC/PEI beads present a better recovery performance compared to LD/PEI beads when applied for the treatment of synthesized leaching liquors.

Composite PVDF-TiO₂ membranes are studied extensively in literature as effective anti-fouling membranes with photocatalytic properties. Yet, a full understanding of how preparation parameters affect the final membrane structure, properties and performance has not been realized. In this study, PVDF-TiO₂ membranes (20 wt% TiO₂/PVDF) were fabricated via the non-solvent-induced phase separation (NIPS) method with an emphasis on the preparation temperature. Then, a systematic approach was employed to study the evolution of the membrane formation process and membrane properties when the preparation temperature changed, as well as to establish a link between them. Typical asymmetric membranes with a high porosity were obtained, along with a vast improvement in the permeate flux compared to the neat PVDF membranes, but a reduction in mechanical strength was also observed. Interestingly, upon the increase in preparation temperature, a significant transition in membrane morphology was observed, notably the gradual diminution of the finger-like macrovoids. Other membrane properties such as permeability, porosity, thermal and mechanical properties, and compression behavior were also influenced accordingly. Together, the establishment of the ternary phase diagrams, the study of solvent–nonsolvent exchange rate, and the direct microscopic observation of membrane formation during phase separation, helped explain such evolution in membrane properties.

The incorporation of brown algae into biopolymer beads or foams for metal sorption has been previously reported. However, the direct use of these biomasses for preparing foams is a new approach. In this study, two kinds of porous foams were prepared by ionotropic gelation using algal biomass (AB, Laminaria digitata) or alginate (as the reference) and applied for Pb(II) sorption. These foams (manufactured as macroporous discs) were packed in filtration holders (simulating fixed-bed column) and the system was operated in either a recirculation or a one-pass mode. Sorption isotherms, uptake kinetics and sorbent reuse were studied in the recirculation mode (analogous to batch system). In the one-pass mode (continuous fixed-bed system), the influence of parameters such as flow rate, feed metal concentration and bed height were investigated on both sorption and desorption. In addition, the effect of Cu(II) on Pb(II) recovery from binary solutions was also studied in terms of both sorption and desorption. Sorption isotherms are well fitted by the Langmuir equation while the pseudo-second order rate equation described well both sorption and desorption kinetic profiles. The study of material regeneration confirms that the reuse of the foams was feasible with a small mass loss, even after 9 cycles. In the one-pass mode, for alginate foams, a slower flow rate led to a smaller saturation volume, while the effect of flow rate was less marked for AB foams. Competitive study suggests that the foams have a preference for Pb(II) over Cu(II) but cannot selectively remove Pb(II) from the binary solution.