Ba₂Mg_0.4Co_1.6Fe₁₂O₂₂ was prepared in powder form by sonochemical co-precipitation and examined by X-ray diffraction, Mössbauer spectroscopy and magnetization measurements. Careful XRD data analyses revealed the Y-type hexaferrite structure as an almost pure phase with a very small amount of CoFe₂O₄ as an impurity phase (about 1.4%). No substantial changes were observed in the unit cell parameters of Ba₂Mg_0.4Co_1.6Fe₁₂O₂₂ in comparison with the unsubstituted compound. The Mössbauer parameters for Ba₂Mg_0.4Co_1.6Fe₁₂O₂₂ were close to those previously found (within the limits of uncertainty) for undoped Ba₂Mg₂Fe₁₂O₂₂. Isomer shifts (0.27–0.38 mm/s) typical for high-spin Fe³⁺ in various environments were evaluated and no ferrous Fe²⁺ form was observed. However, despite the indicated lack of changes in the iron oxidation state, the cationic substitution resulted in a significant increase in the magnetization and in a modification of the thermomagnetic curves. The magnetization values at 50 kOe were 34.5 emu/g at 4.2 K and 30.5 emu/g at 300 K. The zero-field-cooled (ZFC) and field-cooled (FC) magnetization curves were measured in magnetic fields of 50 Oe, 100 Oe, 500 Oe and 1000 Oe, and revealed the presence of two magnetic phase transitions. Both transitions are shifted to higher temperatures compared to the undoped compound, while the ferrimagnetic arrangement at room temperature is transformed to a helical spin order at about 195 K, which is considered to be a prerequisite for the material to exhibit multiferroic properties.

We report results on the structural and microwave properties and magnetic phase transitions in polycrystalline Sr₃Co₂Fe₂₄O₄₁ hexaferrite synthesized by sol-gel auto-combustion and acting as a filler in a composite microwave absorbing material. The zero-field-cooled (ZFC) and field-cooled (FC) magnetization curves revealed a change in the magnetization behavior at 293 K. The reflection losses in the 1–20 GHz range of the Sr₃Co₂Fe₂₄O₄₁ powder dispersed homogeneously in a polymer matrix of silicon rubber were investigated in both the absence and presence of a magnetic field. In the latter case, a dramatic rise in the attenuation was observed. The microwave reflection losses reached the maximum value of 32.63 dB at 17.29 GHz in the Ku-band. The sensitivity of the microwave properties of the composite material to the external magnetic field was manifested by the appearance of new reflection losses maxima. At a fixed thickness t_m of the composite, the attenuation peak frequency can be adjusted to a certain value either by changing the filling density or by applying an external magnetic field.

Here, we report results on the magnetic and microwave properties of polycrystalline Y-type hexaferrite synthesized by sol-gel auto-combustion and acting as a filler in a composite microwave-absorbing material. The reflection losses in the 1–20 GHz range of the Y-type hexaferrite powder dispersed homogeneously in a polymer matrix of silicon rubber were investigated in the absence and in the presence of a magnetic field. A permanent magnet was used with a strength of 1.4 T, with the magnetic force lines oriented perpendicularly to the direction of the electromagnetic wave propagation. In the case of using an external magnetic field, an extraordinary result was observed. The microwave reflection losses reached a maximum value of 35.4 dB at 5.6 GHz in the Ku-band without a magnetic field and a maximum value of 21.4 dB at 8.2 GHz with the external magnetic field applied. The sensitivity of the microwave properties of the composite material to the external magnetic field was manifested by the decrease of the reflected wave attenuation. At a fixed thickness, t_m, of the composite, the attenuation peak frequency can be adjusted to a certain value either by changing the filling density or by applying an external magnetic field.

This article identifies important components and describes the safe practices in implementing radiation protection and radioactive waste management programmes, and in their optimisation at the Nuclear Scientific Experimental and Educational Centre with research reactor IRT at INRNE-BAS. It covers the instrumentation and personal protective equipment and organisational issues related to the continuous site monitoring. The reactor is under major reconstruction and the measures applied to radiation monitoring of environment and working area focused on restricting the radiation exposure of the staff as well as compliance with international good practices related to the environmental and public radiation safety requirements are also addressed.