This study investigates a novel approach to moderate-temperature carbon capture by examining the enhanced performance of thermally pre-treated dolomite. To obtain mixed oxides, dolomite samples were prepared via calcination in a quartz cylindrical furnace under an ambient atmosphere at 900 °C, and subsequently thermally pre-treated under an inert (argon) stream at 650 °C. Characterization of the as-prepared samples involved morphological, structural, textural, and optical features examined through XRD, BET, SEM-EDS, FT-IR, and RAMAN, XPS, and UV-vis spectroscopy, whereas TGA and subsequent multicyclic tests were used to study the CO₂ sorption. The dolomite sample calcined at 900 °C for 60 min, and after being activated under an inert atmosphere (argon), labeled PCD60Act, exhibited the highest CO₂ uptake of 0.477 g_CO2/g_sorbent; after 15 sorption–regeneration cycles, it still retained a CO₂ uptake of 0.38 g_CO2/g_sorbent at 650 °C, and it was also successfully regenerated at this moderate temperature, demonstrating 84% capture capacity retention. These remarkable results are explained by the crystalline defects generated during the thermal pre-treatments of the dolomite. This research offers valuable perspectives on the viability of employing thermally pre-treated dolomite as an inexpensive, thermally stable, and moderate-temperature regenerable CaO-based sorbent for applications in CO₂ removal in the context of integrated carbon capture and conversion (ICCC) for the production of high-purity hydrogen.

Achieving net-zero carbon emissions, this study introduces a sustainable pathway for reducing strontium sulfate (SrSO₄) and celestite ore to strontium sulfide (SrS) using biofuels (biomethane, bioethanol) derived from agro-industrial waste and green hydrogen. Traditional SrSO₄ reduction methods, which rely on fossil-derived reductants like coal and operate at energy-intensive temperatures (1100–1200 °C), generate significant greenhouse gases and toxic byproducts, highlighting the need for eco-friendly alternatives. Experimental results demonstrate that bioethanol outperformed other reductants, achieving 97% conversion of synthetic SrSO₄ at 950 °C within 24 min and 74% conversion of natural celestite ore over 6 h. Remarkably, this bioethanol-driven process matches the energy efficiency of the conventional black ash method while enabling carbon neutrality through renewable feedstock utilization, reducing CO₂ emissions by 30–50%. By valorizing agro-industrial waste streams, this strategy advances circular economy principles and aligns with Mexico’s national agenda for sustainable industrial practices, including its commitment to decarbonizing heavy industries. This study contributes to sustainable development goals and offers a scalable solution for decarbonizing strontium compound production in the chemical industry.