With the fast development of the cold chain transportation industry, the traditional refrigeration method results in significant energy consumption. To address the national call for energy saving and emission reduction, the search for a new type of energy storage material has already become a future development trend. According to the national standard GB/T28577 for the classification and basic requirements of cold chain logistics, the temperature in frozen logistics is typically below −18 °C. In this study, n-undecane with a phase change temperature of −26 °C is chosen as the core material of microcapsules. Poly(methyl methacrylate) is applied as the shell material, with n-undecane microcapsules being prepared through suspension polymerization for phase change cold storage materials (MEPCM). Using characterization techniques including SEM, DSC, FTIR, and laser particle size analysis, the effects of three types of emulsifiers (SMA, Tween-80, Tween-80/span-80 (70/30)), SMA emulsifier dosage, core–shell ratio, and emulsification rate on the thermal performance and micro-surface morphology of n-undecane/PMMA microcapsules were studied. The results indicate that when comparing SMA, Tween-80, and Tween-80/span-80 (70/30) as emulsifiers, the dodecane/PMMA microcapsules prepared with SMA emulsifier exhibit superior thermal performance and micro-surface morphology, possessing a complete core–shell structure. The optimal microstructure and the highest enthalpy of phase change, measuring 120.3 kJ/kg, are achieved when SMA is used as the emulsifier with a quantity of 7%, a core-to-wall ratio of 2.5:1, and an emulsification speed of 2000 rpm. After 200 hot and cold cycles, the enthalpy of phase change decreased by only 18.6 kJ/kg, indicating the MEPCM thermal performance and cycle life. In addition, these optimized microcapsules exhibit favorable microstructure, uniform particle size, and efficient energy storage, making them an excellent choice for the refrigeration and freezing sectors.

Microencapsulated phase-change materials (MPCMs) with excellent thermal properties for low-temperature cold storage were developed in this study. Using 1-decanol as the core and methyl methacrylate as the shell precursor, the effects of emulsifier type and ultrasonic emulsification conditions were investigated. Styrene-maleic anhydride copolymer served effectively as a protective colloid emulsifier, producing MPCMs with high enthalpy and a well-defined, uniform microstructure. Under optimal conditions of 5 wt% emulsifier content relative to the oil phase, an ultrasonic power of 375 W, and an emulsification time of 12 min, the MPCMs exhibited a phase-change enthalpy of 126.7 kJ/kg. To further improve the thermal properties, a binary eutectic mixture was prepared by combining 1-decanol and 1-tetradecane at an optimal molar ratio (51.1:48.9). This binary-core MPCM showed a higher storage enthalpy (144.3 kJ/kg), with an increase of 13.9% compared to the single-core material (1-decanol). It also exhibited improved microstructural uniformity due to the stabilizing role of 1-tetradecane. These optimized MPCMs demonstrate phase-transition temperatures particularly suitable for low-temperature thermal storage, providing a practical and innovative technical solution for cold-chain logistics and vaccine refrigeration applications.

In this paper, the effect of waste rock-wool dosage on the workability, mechanical strength, abrasion resistance, toughness and hydration products of PVA and steel fiber-reinforced mortars was investigated. The results showed that the fluidity of the mortar gradually decreased with the increase in the dosage of waste rock wool, with a maximum reduction of 10% at a dosage of 20%. The higher the dosage of waste rock wool, the greater the reduction in compressive strength. The effect of waste rock wool on strength reduction decreases with increasing age. When the dosage of waste rock wool was 10%, the 28 days of flexural and compressive strengths were reduced by 4.73% and 10.59%, respectively. As the dosage of waste rock wool increased, the flexural-to-compressive ratio increased, and at 20%, the maximum value of 28 days of flexural-to-compressive ratio was 0.210, which was increased by 28.05%. At a 5% dosage, the abraded volume was reduced from 500 mm³ to 376 mm³—a reduction of 24.8%. Waste rock wool only affects the hydration process and does not cause a change in the type of hydration products. It promotes the hydration of the cementitious material system at low dosages and exhibits an inhibitory effect at high dosages.

Methyl methacrylate (MMA) material is considered to be a suitable material for repairing concrete crack, provided that its large volume shrinkage during polymerization is resolved. This study was dedicated to investigating the effect of low shrinkage additives polyvinyl acetate and styrene (PVAc + styrene) on properties of the repair material and further proposes the shrinkage reduction mechanism based on the data of FTIR spectra, DSC testing and SEM micrographs. The results showed that PVAc + styrene delayed the gel point during the polymerization, and the formation of two-phase structure and micropores compensated for the volume shrinkage of the material. When the proportion of PVAc + styrene was 12%, the volume shrinkage could be as low as 4.78%, and the shrinkage stress was reduced by 87.4%. PVAc + styrene improved the bending strength and fracture toughness of most ratios investigated in this study. When 12% PVAc + styrene was added, the 28 d flexural strength and fracture toughness of MMA-based repair material were 28.04 MPa and 92.18%, respectively. After long-term curing, the repair material added with 12% PVAc + styrene showed a good adhesion to the substrate, with a bonding strength greater than 4.1 MPa and the fracture surface appearing at the substrate after the bonding experiment. This work contributes to the obtaining of a MMA-based repair material with low shrinkage, while its viscosity and other properties also can meet the requirements for repairing microcracks.

In order to further optimize the performance of PMMA (Polymethyl Methacrylate) repair mortar. In this paper, fly ash, talcum powder and wollastonite powder are used as fillers to modify the PMMA repair mortar. The effects of these three fillers on the working performance, mechanical performance and durability of PMMA repair mortar were explored. The study shows that the three fillers have good effect on the bond strength of the repair mortar, in which the fly ash has the best effect on the mechanical performance. The mechanical properties of PMMA repair mortar were best when the amount of fly ash was 60 phr (parts per hundred, representing the amount of the material added per hundred parts of PMMA). At this time, the 28 d compressive strength was 71.26 MPa and the 28 d flexural strength was 28.09 MPa, which increased by 13.31% and 15.33%, respectively. Wollastonite powder had the least negative effect on the setting time of the PMMA repair mortar. When the dosage of wollastonite powder was increased to 100 phr, the setting time was only extended from 65 min to 94 min. When the talc dosage was 60 phr, the best improvement in salt freezing resistance was achieved. After 100 cycles of salt freezing, the mass loss rate and strength loss rate decreased to 0.159% and 4.97%, respectively, which were 75.1% and 37.7% higher than that of the control group. The addition of all three fillers reduced the porosity and the proportion of harmful pores in the mortar. This study contributes to a comprehensive understanding how different types of fillers affect PMMA repair mortars, and it also provides theoretical support for the further development of low-temperature rapid repair mortars.