Organic–inorganic hybrids based on liquid crystalline symmetrical imine (8Z)-N-(4-((Z)-(4-pentylphenylimino)methyl)benzylidene)-4-pentylbenzenamine (AZJ1) with two aliphatic chains and TiO₂ nanomaterials were obtained and investigated taking into account thr crystallographic form of titanium dioxide i.e., anatase versus rutile. The type of TiO₂ influences the mesomorphic properties of imine AZJ1, as observed by differential scanning calorimetry (DSC) and polarizing optical microscopy (POM) techniques. Fourier-Transform Infrared Spectroscopy (FT-IR) was used to investigate the interactions of oxygen vacancies located on the TiO₂ surface with the studied AZJ1 imine together with studying the influence of temperature. Both imine:TiO₂ anatase versus rutile hybrids possessed the highest occupied molecular orbital (HOMO) levels of about −5.39 eV (AZJ1:anatase) and −5.33 eV (AZJ1:rutile) and the lowest unoccupied molecular orbital (LUMO) levels of about −2.24 eV. The presence of TiO₂ in each hybrid did not strongly affect the redox properties of imine AZJ1. Organic devices with the configuration of ITO/TiO₂/AZJ1 (or AZJ1:TiO₂ anatase versus rutile)/Au were fabricated and investigated in the presence and absence of visible light irradiation with a light intensity of 93 mW/cm². Finally, to analyze defects in the constructed organic devices we used thermal imaging and atomic force microscopy (AFM). The addition of TiO₂ in both crystallographic forms has a positive influence on layer-forming properties that manifests itself as a very homogenous heat distribution for the whole sample.

Poly(3,4-ethylenedioxythiophene:poly(styrenesulfonate) (PEDOT:PSS) water and toluene solutions were investigated in detail, taking into consideration their stability, wettability, transparency, and electrochemical properties, along with change polarity caused by dopant. As dopant, methanol, ethanol, and isopropanol were used with different dipole moments (1.70, 1.69, and 1.66 D) and dielectric constants (33.0, 24.5, and 18.0). Three techniques, i.e., spin coating, doctor blade coating, and spray coating, were employed to created PEDOT:PSS layers on glass, glass/indium tin oxide (ITO), and glass/fluorine-doped tin oxide (FTO) substrates with optimized technical parameters for each used equipment. All used PEDOT:PSS water and toluene solutions demonstrated good wetting properties with angles below 30° for all used surfaces. Values of the energy bandgap (Eg) of PEDOT:PSS investigated by cyclic voltammetry (CV) in solution showed increase energy Eg along with addition of alcohol to the mixture, and they were found in the range of 1.20 eV to 2.85 eV. The opposite tendency was found for the Eg value of the PEDOT:PSS layer created from water solution. The storage effect on PEDOT:PSS layers detected by CV affected only the lowest unoccupied molecular orbital (LUMO) level, thereby causing changes in the energy bandgap. Finally, simple devices were constructed and investigated by infrared (IR) thermographic camera to investigate the surface defects on the created PEDOT:PSS layers. Our study showed that a more stable PEDOT:PSS layer without pin-holes and defects can be obtained from water and toluene solutions with isopropanol via the spin coating technique with an optimal speed of 3000 rpm and time of 90 s.

The main idea of this work is based on the latest achievements in the commercialization of sodium-ion (Na-ion) batteries, which constitute a basis of analysis for military applications as energy storage systems. Technical, engineering, and ecological aspects were analyzed to find the optimal solution for using Na-ion batteries for military purposes. When selecting batteries for military applications, the following criteria are required: (a) they are more durable than standard batteries, (b) resistant to fire, (c) cannot explode, (d) cannot emit heat so as not to reveal their position, (e) equipped with safety elements and protective circuits to ensure safety, and (f) have the highest possible energy density, defined as the ratio of capacity to weight. The advantages and challenges of Na-ion batteries are discussed and compared to typical lithium-ion batteries, and also lithium iron phosphate, Ni-Cd, and Ni-MH batteries. The prospects for expanding the practical applications of Na-ion batteries in the military are presented. The unique properties of Na-ion batteries, such as their lower risk of ignition, more excellent thermal stability, and ability to work in extreme conditions, are essential from the point of view of military operations. Additionally, when considering environmental and logistical aspects, sodium-ion batteries may offer more sustainable and cost-effective solutions for the military. Therefore, this work aims not only to present the technological potential of these systems but also to draw attention to their strategic importance for the future of military operations. Battery discharge can result from leaving current receivers switched on or even from a drop in temperature. The discharge current should not exceed 1/10 of the battery capacity (1C). Discharging below the discharge voltage may result in irreversible damage. Sodium-ion batteries are safer to use than their lithium counterparts and allow for discharge to 0 V, eliminating the possibility of uncontrolled thermal discharge due to a short circuit (explosion, ignition), which is particularly important in the military.