Two-dimensional (2D) transition metal nitrides and carbides (MXenes), represented by Ti₃C₂T_x, have broad applications in flexible electronics, electromechanical devices, and structural membranes due to their unique physical and chemical properties. Despite the Young’s modulus of 2D Ti₃C₂T_x has been theoretically predicted to be 0.502 TPa, which has not been experimentally confirmed so far due to the measurement is extremely restricted. Here, by optimizing the sample preparation, cutting, and transfer protocols, we perform the direct in-situ tensile tests on monolayer Ti₃C₂T_x nanosheets using nanomechanical push-to-pull equipment under a scanning electron microscope. The effective Young’s modulus is 0.484 ± 0.013 TPa, which is much closer to the theoretical value of 0.502 TPa than the previously reported 0.33 TPa by the disputed nanoindentation method, and the measured elastic stiffness is ~948 N/m. Moreover, during the process of tensile loading, the monolayer Ti₃C₂T_x shows an average elastic strain of ~3.2% and a tensile strength as large as ~15.4 GPa. This work corrects the previous reports by nanoindentation method and demonstrates that the Ti₃C₂T_x indeed keeps immense potential for broad range of applications.

Fe–Ni hydroxide nanosheets were converted to Fe–Ni phosphide nanoparticle-stack array by low-temperature phosphorization to promote surface area and further improve oxygen evolution reaction activities.