In this work, we report on the fabrication of a novel Organic Double-Layer Supercapacitor (ODLSC) using recycled palm as the substrate and electrodes based on halogenated indium and copper phthalocyanines. The electrodes were characterized using Reflectance, the Kulbeka–Munk function, and Fluorescence. Finally, their electrical behavior was evaluated, and the results were compared with those obtained for a more conventional supercapacitor fabricated on polyethylene terephthalate substrate and using indium tin oxide film for electrodes. Based on the experimental measurements of the fabricated ODLSC, the parameter identification of the classical equivalent circuit model was carried out using the Least Squares of Orthogonal Distances (LSOD) algorithm. The results indicated that the palm supercapacitor exhibited behavior more like that of traditional supercapacitors, as the root square mean error (RMSE) values in the model approximation of the experimental data were in the order of ${10}^{-7}$. Furthermore, the models obtained allowed a determination of the device’s Electrical Impedance Spectroscopy (EIS), revealing that the Palm SC-T1 exhibited capacitive behavior. In contrast, the manufactured Palm SC-T2, PET SC-T1, and PET SC-T2 devices exhibited inductive behavior. All the materials used in this work, such as the substrates, electrodes, separator membranes, and electrolytes, have a high potential to be used in organic supercapacitors.

En este trabajo se presenta la fabricación de dispositivos semiconductores orgánicos, depositados sobre sustratos de hoja de palma reciclada, y ftalocianinas halogenadas de cobre e indio, F16CuFt e InFtCl, como electrodos. Para la fabricación de los dispositivos, los sustratos de palma se prepararon en sus dimensiones y superficie, con la finalidad de ser recubiertos con carbón conductor. Los electrodos F16CuFt e InFtCl se depositaron como películas delgadas mediante evaporación a alto vacío, y los dispositivos fabricados se caracterizaron mediante espectrofotometría ultravioleta–visible y fluorescencia. A partir de la reflectancia, se determinó la función de Kubelka–Munk con el fin de obtener el band gap óptico, parámetro fundamental para evaluar la capacidad semiconductora de las ftalocianinas. Posteriormente, se evaluó el comportamiento eléctrico mediante el método de cuatro puntas colineal. La evaluación eléctrica se realizó en condiciones de iluminación natural, en oscuridad y bajo radiación de diferentes longitudes de onda, presentando un comportamiento distinto para cada electrodo.

This study presents the fabrication of composite photoelectrodes containing halogenated phthalocyanines (F₁₆CuPc and MnPcCl) embedded in polymeric matrices of PEDOT:PSS (poly(2,3-dihydrothieno-1,4-dioxin)-poly(styrenesulfonate)) and PLA (polylactic acid biopolymer). These composites were deposited on PET, palm leaf, and wheat bagasse recyclable substrates, and were morphologically characterized. The reflectance for F₁₆CuPc/PEDOT:PSS is less than 8.5%, and that for MnPcCl/PLA changes depending on the substrate, ranging between 10% and 40%. Additionally, in the case of F₁₆CuPc/PEDOT:PSS, the Kubelka–Munk band gap is 3.7 eV, and in the case of F₁₆CuPc/PEDOT:PSS, the band gap varied between 2.85 and 3.47 eV. The composites were evaluated as electrodes in bio-based sustainable devices, fabricated with commercially available paper towels used as an organic membrane separator. The palm-device showed the best performance throughout its charge and discharge cycle. The device improves its performance at high speeds and reaches its highest peak at 100 mV s⁻¹ with 3.14 × 10⁴ μA. On the other hand, the greatest thermal stability for the composites is for those deposited onto bagasse substrate, reaching up to 220 °C and 357 °C for F₁₆CuPc/PEDOT:PSS and MnPcCl/PLA, respectively. Also, these composites exhibit charge–discharge behavior when studied in bio-based sustainable devices and can be used as electrodes.