The phosphate industry produces huge volumes of waste (hundred million tons per year). These wastes are generally surface landfilled, leading to significant environmental impacts and a large footprint. The current practices of phosphate waste management, the typology of the waste streams and their characteristics, and finally their potential applications are reviewed. All the waste streams generated during the life cycle of phosphoric acid production going from the extraction of phosphate rock to its enrichment and transformation are considered. Great circularity opportunities have been identified and they aim (i) to recover the residual phosphorus and other critical minerals and metals, and (ii) to consider phosphate wastes as alternative resources in the civil engineering and building sectors. The purpose is to shift from linear thinking to circular thinking where synergy between different mining and other industries is highly encouraged. By doing so, opportunities to safeguard natural resources and to minimize the environmental and societal impacts are limitless. However, many challenges are still limiting this shift: economic and technical constraints, societal and policy-makers’ awareness, regulation harmonization and finally knowledge gaps. More efforts and investment in research and development are still required to reach the zero-waste target.

Nowadays, the global brick industry utilizes billions of cubic meters of clay soil annually, resulting in the massive consumption of non-renewable resources. This study explores the viability of utilizing red marl from phosphate mining waste rocks for fired brick production. Ecofriendly fired bricks produced from 100% side streams (red marly clays (RM) and marble waste powder (MWP)) were prepared, pressed, dried at 105 °C, and then fired at 1100 °C for 1 h. The effects of marble waste powder addition (up to 30 wt%) on the physical, mechanical, mineralogical, and microstructural properties of the fired bricks were explored. The main results show that fired bricks with high compressive strength of a maximum of 39 MPa could be prepared with a mixture of red marl and 10 wt% of marble waste powder. The thermal conductivity was decreased by marble waste addition (from 0 to 30%) and was reduced from 0.93 W/m.k to 0.53 W/m.k; however, the compressive strength was also decreased to reach a minimum of 17 MPa. The firing shrinkage and density were also reduced with 30% marble waste by 41% and 18%, respectively. Therefore, red marly clays and marble waste could be promising raw materials for eco-fired brick production.