A novel method for the rapid modification of fullerene for subsequent enzyme attachment to create a potentiometric biosensor is presented. Urease was immobilized onto the modified fullerene nanomaterial. The modified fullerene-immobilized urease (C₆₀-urease) bioconjugate has been confirmed to catalyze the hydrolysis of urea in solution. The biomaterial was then deposited on a screen-printed electrode containing a non-plasticized poly(n-butyl acrylate) (PnBA) membrane entrapped with a hydrogen ionophore. This pH-selective membrane is intended to function as a potentiometric urea biosensor with the deposition of C₆₀-urease on the PnBA membrane. Various parameters for fullerene modification and urease immobilization were investigated. The optimal pH and concentration of the phosphate buffer for the urea biosensor were 7.0 and 0.5 mM, respectively. The linear response range of the biosensor was from 2.31 × 10⁻³ M to 8.28 × 10⁻⁵ M. The biosensor’s sensitivity was 59.67 ± 0.91 mV/decade, which is close to the theoretical value. Common cations such as Na⁺, K⁺, Ca²⁺, Mg²⁺ and NH₄⁺ showed no obvious interference with the urea biosensor’s response. The use of a fullerene-urease bio-conjugate and an acrylic membrane with good adhesion prevented the leaching of urease enzyme and thus increased the stability of the urea biosensor for up to 140 days.

The importance of dye sensitized solar cells (DSSCs) as a low-cost and environmentally friendly photovoltaic (PV) technology has prompted many researchers to improve its efficiency and durability. The realization of these goals is impossible without taking into account the importance of the materials in DSSCs, so the focus on the preparation/deposition methods is essential. These methods can be either chemical or physical. In this study, the chemical applied methods that utilize chemical reaction to synthesize and deposit the materials are covered and categorized according to their gas phase and liquid phase precursors. Film processing techniques that can be used to enhance the materials' properties postpreparation are also included for further evaluation in this study. However, there is a variety of consideration, and certain criteria must be taken into account when selecting a specific deposition method, due to the fact that the fabrication conditions vary and are unoptimized.

Dye sensitized solar cells (DSSCs) have attracted numerous research, especially in the context of enhancing their efficiency and durability, due to the low-cost and environmentally friendly nature of photovoltaic (PV) technology. The materials in DSSCs are vital towards the realization of these goals, since many of the important components are influenced by their respective preparation and deposition methods. This review aims to detail the research and development aspects of the different physical methods with the purpose of evaluating their prospects and corresponding limitations. The diversity of consideration and criteria includes thin film applications, material characteristics, and process technology that need to be taken into account when selecting a specific deposition method. Choosing a deposition method is not as simple as it seems and is rendered quite complicated due to various factors. Usually, a researcher will evaluate techniques based on factors such as the different preparations and deposition technology with materials’ and substrates’ type, specified applications, costs, and efficiencies.