The inefficiency of unreinforced concrete beams as flexural members poses a challenge because concrete’s tensile strength is significantly lower than its compressive strength. In response to this challenge, reinforcement bars are commonly employed near the tension zone of reinforced concrete (RC) beams. Nonetheless, structures constructed with RC face challenges such as reduced live load capacity, concrete deterioration, and the corrosion of reinforcement bars over time. To address this, ongoing research is exploring maintenance and retrofitting techniques using high-strength, lightweight fiber-reinforced polymer (FRP) composite materials such as carbon fiber-reinforced polymer (CFRP) and glass fiber-reinforced polymer (GFRP). In this study, the flexural performance of corroded RC beams was enhanced through retrofitting with CFRP plates and sheets. The corroded RC beams were fabricated using an applied-current method with a 5% NaCl solution to induce a 10% target corrosion level under controlled laboratory conditions. Flexural tests were conducted to evaluate the structural performance, failure modes, load–displacement relationships, and energy dissipation capacities. The results showed that CFRP reinforcement mitigates the adverse effects of corrosion-induced reduction in rebar cross-sectional areas, leading to increased stiffness and improved load-carrying capacity. In particular, CFRP reinforcement increased the yield load by up to 36.5% and the peak load by up to 90% in corroded specimens. The accumulated energy dissipation capacity also increased by 92%. These enhancements are attributed to the effective load-sharing behavior between the corroded rebar and the CFRP reinforcement.

This study investigates the axial–flexural behavior of steel fiber–reinforced concrete (SFRC) columns under combined constant axial load and monotonic lateral loading. Nine column specimens with different axial load ratios (0.0, 0.10, and 0.20) and steel fiber contents (0.0%, 0.5%, and 1.0%) were tested under monotonic loading to evaluate their failure modes, load–deflection behavior, ductility, and energy absorption capacity. In addition, a sectional P–M interaction analysis was performed to examine the influence of steel fiber inclusion on flexural strength under different axial compression levels. The interaction diagrams indicated that steel fibers expanded the flexural strength envelope, with a more pronounced enhancement in the low-axial-load region. The test results revealed that increasing the axial load ratio enhanced the specimens’ peak load capacity but reduced their ductility, leading to a brittle failure mode. Conversely, the incorporation of steel fiber improved the crack distribution, delayed crack propagation, and enhanced both ductility and energy absorption, particularly under moderate axial load conditions. The failure modes were characterized generally by flexural cracking and localized crushing in the compression zone, with the specimens that contained steel fiber exhibiting a more gradual post-peak load response than the specimens without steel fiber. The energy absorption capacity, quantified as the area under the load–deflection curve, was maximized when the axial load ratio of 0.10 was used in tandem with steel fiber reinforcement, indicating an optimal balance between strength and ductility. Overall, steel fiber inclusion improved deformation capacity and energy absorption under monotonic loading, particularly at low-to-moderate axial load ratios.

Research on the long-term durability of concrete has continued due to its widespread application in construction. Freeze–thaw cycles significantly impact concrete durability, particularly in regions with harsh climates. While most studies focus on the material properties of concrete, limited research has addressed the performance degradation of reinforced concrete structures. This study investigates the freeze–thaw resistance of RC beams made with 35 MPa concrete, with particular emphasis on the influence of air content on flexural performance. RC beams were exposed to freeze–thaw cycles using the air freeze–thaw method and the ASTM C666/C666M-15 water freeze–thaw method. Their flexural behavior was evaluated through four-point bending tests. The results showed that low-air-content RC beams exhibited notable reductions in yield load and energy absorption capacity after freeze–thaw cycles, indicating decreased strength and ductility. Conversely, RC beams with appropriate or high air content exhibited minimal reductions, demonstrating superior freeze–thaw resistance. These findings underscore the importance of optimizing air content to enhance the durability of RC structures in harsh environmental conditions.