SCIEPublish is an international open-access journal publishing service provider run by SCIE Publishing Limited, dedicated to supporting and inspiring scientists or institutions/societies who aspire to publish high-quality journals.

Hastelloy is widely used in the manufacturing of high-temperature components in the aerospace industry because of its high strength and corrosion-resistant physical properties, as well as its ability to maintain excellent mechanical properties at high temperatures. However, with developments in science and technology, the amount of available components for use in high-temperature and corrosive environments is increasing, their structures are becoming more complex and varied, and requirements with regard to the surface quality of the components has also become more stringent. The integration of cold plasma (CP) and nano-lubricant minimum quantity lubrication (NMQL), within a multi-physics coupling-assisted micro-grinding process (CPNMQL), presents a promising strategy to overcome this bottleneck. In this paper, micro-grinding of Hastelloy C-276 was performed under dry, CP, NMQL, and CPNMQL conditions, respectively. Contact angle testing, X-ray photoelectron spectroscopy (XPS) analysis, and nano-scratch experiments were used to investigate the mechanism of CPNMQL and to compare the micro-milling performance under different cooling and lubrication conditions employing various characteristics such as grinding temperature, surface roughness, and 3D surface profile. The results showed that at different micro-grinding depths, the micro-grinding temperature and surface roughness were significantly reduced under CP, NMQL, and CPNMQL conditions compared to dry friction. Among them, CPNMQL showed the best performance, with 53.4% and 54.7% reductions in temperature and surface roughness, respectively, compared to the dry condition.

H-BN spherical nanoparticles, known as white graphene, have good anti-wear properties, long service life, chemical inertness, and stability, which provide superior lubricating performance as a solid additive item to nanofluids. However, the poor dispersion stability of h-BN nanoparticles in nanofluids is a bottleneck that restricts their application. Currently, to prepare h-BN nanofluids with good dispersion stability, a cold plasma (CP) modification of h-BN nanoparticles is proposed in this study. In this research, h-BN nanofluid with added surfactant (SNL), CP-modified h-BN nanofluid with N₂ as the working gas (CP(N₂)NL), and CP-modified h-BN nanofluid with O₂ as the working gas (CP(O₂)NL) were prepared, separately. The mechanism of the dispersion stability of CP-modified h-BN nanofluid was analyzed using X-ray photoelectron spectroscopy (XPS), and the performance of CP-modified nanofluid was analyzed based on static observation of nanofluid, kinematic viscosity, and heat transfer properties. Finally, friction and wear experiments were conducted to further analyze the tribological performance of h-BN nanofluids based on the coefficient of friction, 3D surface morphology, surface roughness (Sa), scratches, and micro-morphology. The results show that CP-modified h-BN nanofluid has excellent dispersed suspension stability and can be statically placed for more than 336 h. The CP-modified h-BN nanofluid showed stable friction-reducing, anti-wear, and heat transfer performance, in which the coefficient of friction of h-BN nanofluid was about 0.66 before and after 24 h of settling. The Sa value of the sample was reduced by 31.6–49.2% in comparison with pure cottonseed oil (CO).