In this randomized clinical trial, the clinical and mycological efficacy of Photodynamic Therapy (PDT) was compared with that of topical antifungal therapy for the treatment of denture stomatitis (DS) and the prevalence of Candida species was identified. Patients were randomly assigned to one of two groups (n = 20 each); in the nystatin (NYT) group patients received topical treatment with nystatin (100,000 IU) four times daily for 15 days and in the PDT group the denture and palate of patients were sprayed with 500 mg/L of Photogem(®), and after 30 min of incubation, were illuminated by light emitting-diode light at 455 nm (37.5 and 122 J/cm(2), respectively) three times a week for 15 days. Mycological cultures taken from dentures and palates and standard photographs of the palates were taken at baseline (day 0), at the end of the treatment (day 15) and at the follow-up time intervals (days 30, 60 and 90). Colonies were quantified (CFU/mL) and identified by biochemical tests. Data were analysed by Fisher's exact test, analysis of variance and Tukey tests and κ test (α = 0.05). Both treatments significantly reduced the CFU/mL at the end of the treatments and on day 30 of the follow-up period (p <0.05). The NYT and PDT groups showed clinical success rates of 53% and 45%, respectively. Candida albicans was the most prevalent species identified. PDT was as effective as topical nystatin in the treatment of DS.

Aim: This study firstly evaluated the activity of a silver nanoparticle (AgNPs) solution against Candida albicans and then the effect of incorporation of AgNPs into a denture base acrylic resin on the material’s hydrophobicity, C. albicans adhesion and biofilm formation. Methods and Results: The AgNPs solution was synthesized by chemical reduction and characterized. Minimum inhibitory (MIC) and minimum fungicidal (MFC) concentrations for planktonic cells and sessile cells (MFCs) of the AgNPs solution against C. albicans were determined. Specimens (n = 360) of silver-incorporated acrylic resin at concentrations of 1000, 750, 500, 250 and 30 ppm were also prepared and stored in PBS for 0, 7, 90 and 180 days. Control was acrylic resin without AgNPs (0 ppm). After the storage periods, contact angles were measured and the specimens were used for C. albicans adherence (37°C; 90 min; n = 9) and biofilm formation (37°C; 48 h; n = 9) by XTT reduction assay. MIC, MFC and MFCs values were 3·98, 15·63 and 1000 ppm, respectively. Incorporation of AgNPs reduced the hydrophobicity of the resin. No effect on adherence and biofilm formation was observed. At 90 and 180 days of storage, there was significant increase in adherence and biofilm formation. Conclusions: Although the AgNPs solution had antifungal activity, no effect on C. albicans adherence and biofilm formation was observed after its incorporation into a denture base resin. Significance and Impact of the Study: The synthesized AgNPs solution is a promising antifungal agent, warranting investigations of more efficient methods of incorporation into denture base resins.