The W–Cu composites with nanosized grain boundaries and high effective density were fabricated using a new fast isostatic hot pressing method. A significantly faster method was proposed for the formation of W–Cu composites in comparison to the traditional ones. The influence of both the high temperature and pressure conditions on the microstructure, structure, chemical composition, and density values were observed. It has been shown that W–Cu samples have a polycrystalline well-packed microstructure. The copper performs the function of a matrix that surrounds the tungsten grains. The W–Cu composites have mixed bcc-W (sp. gr. Im $\overline{3}$ m) and fcc-Cu (sp. gr. Fm $\overline{3}$ m) phases. The W crystallite sizes vary from 107 to 175 nm depending on the sintering conditions. The optimal sintering regimes of the W–Cu composites with the highest density value of 16.37 g/cm³ were determined. Tungsten–copper composites with thicknesses of 0.06–0.27 cm have been fabricated for the radiation protection efficiency investigation against gamma rays. It has been shown that W–Cu samples have a high shielding efficiency from gamma radiation in the 0.276–1.25 MeV range of energies, which makes them excellent candidates as materials for radiation protection.

For the first time shields based on W–Bi₂O₃ composites against gamma-rays were sintered via the hot isostatic pressing. The calculation results showed that the composites better than Pb and Bi, which makes them promising for shielding application.

The results of studies on the wettability properties and preparation of porous anodic alumina (PAA) membranes with a 3.3 ± 0.2 μm thickness and a variety of pore sizes are presented in this article. The wettability feature results, as well as the fabrication processing characteristics and morphology, are presented. The microstructure effect of these surfaces on wettability properties is analyzed in comparison to outer PAA surfaces. The interfacial contact angle was measured for amorphous PAA membranes as-fabricated and after a modification technique (pore widening), with pore sizes ranging from 20 to 130 nm. Different surface morphologies of such alumina can be obtained by adjusting synthesis conditions, which allows the surface properties to change from hydrophilic (contact angle is approximately 13°) to hydrophobic (contact angle is 100°). This research could propose a new method for designing functional surfaces with tunable wettability. The potential applications of ordinary alumina as multifunctional films are demonstrated.