The unique structures and properties of natural organisms provide abundant inspiration for surface modification research in materials science. In this paper, the tribological advantages of radial ribs found on shell surfaces were combined with laser cladding to address challenges in material surface strengthening. Laser cladding technology was used to fabricate bionic units on the surface of 20CrMnTi steel. The alloy powder consisted of a Ni-based alloy with added WC particles. The influence of laser power (1.0 kW–3.0 kW) on the dimensions, microstructure, hardness, surface roughness, and tribological properties of the bionic units was investigated to enhance the tribological performance of the Ni60/WC bionic unit. The microstructure, phase composition, hardness, and tribological behavior of the bionic units were characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD), a microhardness tester, and a wear tester. Experimental results show that the dimensions of the bionic units increased with laser power. However, beyond a certain threshold, the growth rate of the width and height gradually slowed due to heat conduction and edge cooling effects. The microstructure primarily consisted of equiaxed and dendritic crystals, with grain refinement observed at higher laser powers. The addition of WC resulted in average hardness values of 791 HV_0.2, 819 HV_0.2, 835 HV_0.2, and 848 HV_0.2 across the samples. This enhancement in hardness was attributed to dispersion strengthening and grain refinement. Increasing the laser power also reduced the surface roughness of the bionic units, though excessively high laser power led to a roughness increase. The presence of WC altered the wear mechanism of the bionic units. Compared to the wear observed in the N60 sample, the wear amount of the WC-containing samples decreased by 73.7%, 142.1%, 157.5%, and 263.1%, respectively. Hard WC particles played a decisive role in enhancing tribological performance of the bionic unit.

In recent years, the field of bionic engineering has advanced at a remarkable pace. Numerous engineering challenges have been addressed through inspiration drawn from biological organisms in nature. In this paper, laser cladding was employed to fabricate a bionic unit inspired by the radial ribs of the bivalve shell surface morphology on 20CrMnTi steel, with the aim of enhancing its wear performance. The metallic powder used in the experiments was prepared by blending Ni60 alloy powder with tungsten carbide (WC) in a predetermined ratio. The WC content was maintained within a mass percentage range of 15% to 60% in the composite powder system. The microstructure and properties of the bionic unit were characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD), and a hardness tester, while its dry sliding wear resistance was evaluated using a block-on-ring tribometer. The influence of the WC content on the microstructure, hardness, surface roughness, and wear performance of the bionic unit was investigated. The experimental results revealed that the bionic unit exhibited a dual microstructure comprising equiaxed crystals and fine dendritic structures. The incorporation of WC induced pronounced grain refinement, while the dispersed WC particles formed effective metallurgical bonding with the Ni-substrate. A positive correlation was observed between the WC content and hardness, with peak hardness reaching 1008 HV_0.2 at 60% WC. Tribological analysis demonstrated a wear mechanism transition from dominant abrasive wear to a hybrid abrasive–adhesive wear. The wear volume of the bionic unit decreased with increasing WC content, and the extent of damage was reduced.

Ni/B₄C/TiC coating was prepared using laser cladding technology with 45 steel as substrate material. The effects of different scanning speeds on phase composition, microstructure, microhardness, and tribological properties were investigated. It was found that the coating is primarily composed of Fe₃B, Fe₃C, B₂Fe₃Ni₃, TiC, and solid solution of [Fe, Ni]. TiC particles are not completely dissolved, which promotes grain refinement. The microhardness increases with the increase in scanning speed and reaches the maximum value at 240 mm/min. The wear resistance test revealed that the coating exhibited the best wear resistance at 240 mm/min. The main wear mechanisms were fatigue wear, abrasive wear, and a small amount of oxidative wear.