In this study we present an application of wood biomass—alder wood char—as the carbon precursor for the synthesis of novel and sustainable nitrogen-doped activated-carbon-supported nickel nanoparticle catalyst (AWC-Ni-N) for hydrazine oxidation. For comparison, the wood-based carbon material doped with nitrogen only (AWC-N) was also synthesized. Extensive characterization, including SEM, Raman spectroscopy, XPS, and XRD revealed the catalysts’ microstructure and properties. Electrochemical testing demonstrated that the AWC-Ni-N catalyst significantly enhanced the efficiency of the hydrazine oxidation reaction. In addition, direct N₂H₄-H₂O₂ single-fuel-cell tests were conducted using the prepared AWC-N and AWC-Ni-N catalysts as the anodes and cathodes. Peak power densities of up to 10.8 mW cm⁻² were achieved at 25 °C, corresponding to a current density of 27 mA cm⁻² and a cell voltage of 0.4 V when the AWC-Ni-N catalyst was used as both the anode and cathode. Furthermore, the peak power density increased by approximately 1.6 and 2.9 times, respectively, when the operating temperature was raised from 25 °C to 55 °C for the AWC-N and AWC-Ni-N catalysts. Overall, the AWC-N and AWC-Ni-N catalysts demonstrated significant potential as anode and cathode materials in direct N₂H₄-H₂O₂ fuel cells.

In this study we present an application of wood biomass - alder wood char as the carbon precursor for the synthesis of novel and sustainable nitrogen-doped activated carbon supported nickel nanoparticle catalyst (AWC-Ni-N) for hydrazine oxidation. For comparison, the wood-based carbon material doped with nitrogen only (AWC-N) was also synthesized. Extensive characterization, including SEM, Raman spectroscopy, XPS, and XRD revealed the catalysts' microstructure and properties. Electrochemical testing demonstrated that the AWC-Ni-N catalyst significantly enhanced the efficiency of the hydrazine oxidation reaction. In addition, direct N2H4-H2O2 single fuel cell tests were conducted using the prepared AWC-N and AWC-Ni-N catalysts as the anodes and cathodes. Peak power densities of up to 10.8 mW cm⁻² were achieved at 25 °C, corresponding to a current density of 27 mA cm⁻² and a cell voltage of 0.4 V when the AWC-Ni-N catalyst was used as both the anode and cathode. Furthermore, the peak power density increased by approximately 1.6 and 2.9 times, respectively, when the operating temperature was raised from 25 °C to 55 °C for the AWC-N and AWC-Ni-N catalysts. Overall, the AWC-N and AWC-Ni-N catalysts demonstrate significant potential as anode and cathode materials in direct N2H4-H2O2 fuel cells.

In this study the development of sustainable electrocatalysts for clean energy by modifying biomass-derived activated carbon with nitrogen and transition metals is presented. Activated carbon (AWC) was synthesized using alder wood char as a precursor, while nitrogen and cobalt or copper nanoparticles were incorporated with the aim to create efficient materials for hydrazine oxidation (HzOR) and direct hydrazine-hydrogen peroxide fuel cells (DHHPFC, N2H4–H2O2). The composition, structure, and surface morphology of the created catalysts were examined using inductively coupled plasma optical emission spectroscopy (ICP-OES), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and scanning electron microscopy and energy dispersive X-ray analysis (SEM/EDX). The activity of the AWC, AWC–Co–N, and AWC–Cu–N catalysts for HzOR was evaluated by cyclic voltammetry (CV) and linear sweep voltammetry (LSV). N2H4–H2O2 fuel cell tests were carried out by employing the catalysts both as the anode and cathode. It was found that all materials retained a hierarchical porous carbon framework, while metal incorporation altered surface compactness Cobalt doping produced well-dispersed Co nanoparticles and abundant Co–N–C coordination sites, whereas Cu introduction resulted in moderately compact structures with uniformly distributed Cu-based nanoparticles. Electrochemical measurements demonstrated that both metal dopants enhanced HzOR activity, with the catalytic performance following the order AWC–Co–N > AWC–Cu–N > AWC. Fuel-cell testing further confirmed this trend: AWC–Co–N achieved the highest maximum power density (30.4 mW cm–2), outperforming AWC–Cu–N (17.7 mW cm–2). These results identify AWC–Co–N as a highly effective bifunctional electrocatalyst for DHHPFCs.

The development of sustainable electrocatalysts for clean energy by modifying biomass-derived activated carbon with nitrogen and transition metals is presented. Activated carbon (AWC) material was obtained using alder wood char as a precursor, while nitrogen and cobalt or copper nanoparticles were incorporated with the aim of creating efficient materials for hydrazine oxidation (HzOR) and direct hydrazine–hydrogen peroxide fuel cells (DHHPFC, N₂H₄–H₂O₂). The composition, structure, and surface morphology of the created materials were examined using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), energy-dispersive X-ray analysis (EDX), and inductively coupled plasma optical emission spectroscopy (ICP-OES). The activity of the AWC, AWC–Co–N, and AWC–Cu–N catalysts for HzOR was investigated using cyclic voltammetry (CV) and linear sweep voltammetry (LSV). N₂H₄–H₂O₂ fuel-cell tests were performed by applying the catalysts as both the anode and cathode. It was found that all materials retained a hierarchical porous carbon framework, while metal incorporation altered surface compactness. Cobalt doping produced well-dispersed Co nanoparticles and abundant Co–N–C coordination sites, whereas Cu introduction resulted in moderately compact structures with uniformly distributed Cu-based nanoparticles. Electrochemical measurements demonstrated that both metal dopants enhanced HzOR activity, with the catalytic performance following the order of AWC–Co–N > AWC–Cu–N > AWC. Fuel-cell testing further confirmed this trend: AWC–Co–N achieved the highest maximum power density (30.4 mW cm⁻²), outperforming AWC–Cu–N (17.7 mW cm⁻²). These results identify AWC–Co–N as a highly effective bifunctional electrocatalyst for DHHPFCs.