A superhydrophobic surface with low adhesion and good wear resistance was fabricated on Ti6Al4V substrates via TiO₂/Ni composite electrodeposition, and subsequently modified with a fluoroalkylsilane (FAS) film. Scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and optical contact angle measurements were used to characterize the surface morphologies, chemical compositions, and surface wettability. The superhydrophobicity of the as-prepared surface results from the fabrication of a hierarchical structure and the assembly of low-surface energy fluorinated components. The as-prepared surface had a water contact angle as high as 162.6° and a sliding angle close to 1.8°. Scratch and abrasion tests showed that the superhydrophobic coating provided a superior wear resistance and stable mechanical abrasion protection. In addition, the influence of processing conditions, such as working voltage, deposited time, pH value, and TiO₂ concentration, was also investigated.

Anti-adhesive Ni coatings with low wettability were successfully fabricated on Ti6Al4V substrates via an electro-brush plating method, and subsequently modified with a fluoroalkylsilane (FAS) film. The surface morphology, chemical compositions, and wettability of the as-prepared coatings were measured using scanning electron microscopy (SEM), X-ray diffractometer (XRD), Fourier transform infrared spectrophotometry (FTIR), and contact angle measurements. The results showed that the surface of Ti6Al4V substrate was endowed with flower-like structures. Each flower-like cluster was constituted by a large number of Ni ions. After surface modification of FAS, the as-prepared Ti6Al4V surface had a water contact angle as high as 151.5°, a sliding angle close to 2.1°, and a solid surface energy as low as 0.97 mJ/m². Potentiodynamic polarization tests showed that the Ni coating could provide a stable corrosion protection. In addition, the effects of processing conditions, such as working voltage, relative velocity, electrolyte concentration, and processing time, were investigated. The mechanism of the adhesive resistance was proposed, and the low wettability of Ti6Al4V surfaces was explained by Cassie–Baxter model. As a result, it was necessary to reduce the fraction of the solid–liquid interface in order to achieve anti-adhesive surface.