The properties of composite materials depend not only on the composition but also on the distribution and orientation of the fillers, i.e., on the internal material architecture. Using the example of two differently composed PEEK-based hybrid materials, the influence of fiber orientation on the tribological behavior of these materials in sliding contact with steel was investigated. The tribological performance of these composites was assessed using a pin-on-disc (PoD) tribometer, testing in a pv range from 0.25 to 32 MPa·m/s. The findings indicate that the printed specimens exhibit a high degree of fiber orientation aligned parallel to the printing paths. Conversely, the injection-molded samples display a three-layered structure across the thickness, with fibers in the skin layers aligned parallel to the injection direction but perpendicular to it in the core. These variations in morphology are evident in both the mechanical properties and the tribological behavior. To describe the influence of the fiber orientation on tribological properties, a model is proposed that allows the prediction of tribological properties for any fiber orientation. Although fiber orientation appears to be the dominant factor in tribological behavior, there is also a clear influence of additional fillers.

The reinforcement of polymers with carbon or glass fibers is the reason for their incredible success as ideal lightweight construction materials. However, one challenge with these materials is their recyclability. True recycling, meaning achieving the same performance level as virgin material, is impossible, especially with mechanical recycling processes, because the reinforcement structure is destroyed. Additionally, thermoplastics undergo molecular degradation and changes in the properties of the materials. Therefore, polymer fiber-reinforced plastics may have an advantage here, as polymer fibers are much more flexible than glass or carbon fibers. We investigated the production and recyclability of microfibrillar composites (MFCs) made of polypropylene (PP) and polyethylene terephthalate (PET). The samples were produced using extrusion-based 3D printing with different parameters, and their morphology and mechanical properties were examined. The samples were crushed, and the residue was fed back into the production line. The process was repeated with the samples produced from regenerate. The results prove that the printing process can be controlled to ensure the presence of fibers in samples made from recycled material. However, it is important to note that the mechanical properties decrease with each additional processing cycle. The choice of manufacturing parameters, especially in 3D printing, is crucial for achieving good properties.