In the present study, DOPO-based alkoxysilane (DOPO-ETES) and amido alkoxysilane (DOPO-AmdPTES) were synthesized by one-step and without by-products as halogen-free flame retardants. The flame retardants were applied on cotton fabric utilizing sol–gel method and pad-dry-cure finishing process. The flame retardancy, the thermal stability and the combustion ehaviour of treated cotton were evaluated by surface and bottom edge ignition flame test (according to EN ISO 15025), thermogravimetric analysis (TGA) and micro-scale combustion calorimeter (MCC). Unlike CO/DOPO-ETES sample, cotton treated with DOPO-AmdPTES nanosols exhibits self-extinguishing ehaviour with high char residue, an improvement of the LOI value and a significant reduction of the PHRR, HRC and THR compared to pristine cotton. Cotton finished with DOPO-AmdPTES reveals a semi-durability after ten laundering cycles keeping the flame-retardant properties unchanged. According to the results obtained from TGA-FTIR, Py-GC/MS and XPS, the major activity of flame retardant occurs in the condensed phase via catalytic induced char formation as physical barrier along with the activity in the gas phase derived mainly from the dilution effect. The early degradation of CO/DOPO-AmdPTES compared to CO/DOPO-ETES, triggered by the cleavage of the weak bond between P and C=O, as the DFT study indicated, provides the beneficial effect of this flame retardant on the fire resistance of cellulose. Graphical abstract

In this work, a pioneering study on the electrical properties of composite carbon nanofibres (CNFs) using current-sensitive atomic force microscopy (CS-AFM) has been demonstrated. CNFs are highly interesting materials which are usable in a wide array of applications e.g. electrode materials for biosensors, lithium ion batteries, fuel cells and supercapacitors. CNFs offer a high specific surface area and thus have a high contact area for charge transfer. CNFs can be produced using spinnable polyacrylonitrile (PAN) as a precursor for carbonisation. For the purpose of developing efficient CNFs with high conductivity and power density, silver nanoparticle (AgNPs)-containing PAN solutions were electrospun to form composite nanofibres which was followed by heat treatment. The applied voltage of the spinning setup and the content of both PAN and the silver nanoparticles in the spinning solution were varied in order to study their influence on the morphology and the electrical properties of the nanofibres. The resultant morphologies and fibre diameters were determined by scanning electron microscopy (SEM). The formation of silver nanoparticles was characterised in solution by UV-visible absorption spectroscopy and dynamic light scattering (DLS), while energy-dispersive X-ray spectroscopy (EDX) and transmission electron microscopy (TEM) were carried out to investigate the presence as well as the average diameter of the AgNPs. The electrical properties of the CNFs were investigated using CS-AFM. This technique gives us the possibility to explore the electrical properties of single fibers and hence derive relationships between the structural features and the electrical properties. Our results show that the composite CNFs have a higher electrical conductivity than the neat CNFs and both the average diameter of the fibers and the electrical conductivity increase with an increasing AgNP content.

In this study, functionalization of PET fabrics with amino groups was achieved by aminolysis. Aminolysis routes were explored using different amine‐based materials including ethylenediamine (EDA), triaminotriethylamine (TAEA) and (3‐aminopropyl)trimethoxysilane (APTMS), (3‐trimethoxy‐silylpropyl)diethylentriamine (TRIAMO) in addition to amino‐functionalized silica nanoparticles as amino‐silane based reagents. The samples were deeply characterized by SEM, AFM, and XPS. Abrasion and tensile tests were carried out to evaluate the mechanical properties of the modified fabrics. Results showed that aminolysis conducted with EDA and TAEA as amino based reagents lower the performances of PET, while dense coatings can be deposited on the fibres by amino silane‐based reagents that act as protective layers. APTMS modified PET presented improved abrasion resistance compared to the native PET. The antibacterial activity of the PET surfaces functionalized with the different amino groups was also evaluated using the gram‐negative bacterium A. fischeri antibacterial assay. The results showed improved antibacterial performances of the native textile treated with APTMS and TAEA based reagents.

Poly- and cyclophosphazenes are excellent flame retardants but currently, are not used as textile finishing agents because water-soluble and permanent washing systems are missing. Here, we demonstrate for the first time, the successful usage of a water-soluble cyclotriphosphazene derivative for textile finishing for cotton, different cotton/polyester, and cotton/polyamide blend fabrics. A durable finish was achieved using a photoinduced grafting reaction. The flame retardant properties of the various fabrics were improved with a higher limiting oxygen index, a reduced heat release rate, and an exhibition of intumescent. Furthermore, the finished textiles passed several standardized flammability tests.

Although current desalination technologies are mature enough and advanced, the shortage of freshwater is still considered as one of the most pressing global issues. Therefore, there is a strong incentive to explore and investigate new potential methods with low energy consumption. We have previously reported that reversible thermally induced sorption/desorption process using polymeric hydrogels hold promise for water desalination with further development. In order to develop a more effective hydrogels architecture, polyelectrolyte moieties were introduced in this work as pendent chains and a thermally responsive polymer as network backbone using reversible addition-fragmentation chain transfer (RAFT) polymerisation. The ability of the comb-type polymeric hydrogels to desalinate water was evaluated. These hydrogels were proved to absorb water with low salinity from brine solution of 2 g L ${}^{-1}$ NaCl and release the absorbed water at relatively low temperature conditions of 50 ${}^{\circ }$ C. The fraction of the grafted polyacrylic acid and the comb-chain length were varied to understand their influence on the swelling/deswelling behaviour for these hydrogels. The ionic fraction in the hydrogels and the resulting hydrophilic/hydrophobic balance are crucial for the proposed desalination process. In contrast, the comb-chain length impacted the swelling behaviour of hydrogels but showed relatively little influence on the dewatering process.