Friction stir processing (FSP) manufacturing technology was used to fabricate medium Mn advanced high-strength steel in this study. The mechanical properties and microstructure of the steel fabricated using FSP were investigated. The steel obtained a total elongation of 35.1% and a tensile strength of 1034.6 MPa, which is about 59% higher than that of the steel without FSP. After FSP, a gradient structure occurs along the thickness direction. Specifically, across the thickness direction from the base material zone to the transition zone and finally to the stirring zone, both the grain size and austenite fraction decrease while the dislocation density increases, which results from the simultaneous effect of severe plastic deformation and recrystallization during FSP. Due to the gradient structure, an obvious difference in the strain across the thickness direction of the steel occurs during the deformation process, resulting in significant hetero-deformation-induced (HDI) strengthening. The deformation mechanism analysis reveals that HDI strengthening and dislocation strengthening are the main factors in the improvement in the strength–ductility balance. The obtained knowledge sheds light on the process of fabricating medium Mn steels with excellent properties using FSP manufacturing technology.

In this paper, we present the effect of austenitizing temperature on the work hardening behavior of air-hardening steel LH800 by evaluating the influence of austenitizing temperature on microstructure evolution and mechanical properties, using Hollomon, Differential Crussard–Jaoul (D_C-J), and Modified C-J (M_C-J) work hardening models. The results reveal that with an increase in austenitizing temperature, there is an increase in the percentage of martensite, along with an increase in the strength and hardness of the LH800 steel; on the other hand, there is a decrease in the plasticity. Austenitized at 825 °C, LH800 steel exhibits its highest strength and good plasticity, with a tensile strength of 897 MPa and an elongation of 13.6%. The comparison between the three strain hardening models revealed that the Hollomon model was the finest fit for the experimental data utilized and could illustrate the work hardening behavior of LH800 steel most suitably. This model manifests a two-stage work hardening mechanism; the first stage is related to the plastic deformation of ferrite phase, while the second stage deals with the co-deformation of ferrite and martensite/bainite phase. As austenitizing temperature increases, the work hardening ability of LH800 steel diminishes at each stage, the transition strain decreases, and the plastic deformation of martensite starts earlier.