In this study, aluminum-doped zinc oxide (Al:ZnO) thin films were grown by high-speed atmospheric atomic layer deposition (AALD), and the effects of air annealing on film properties are investigated. The experimental results show that the thermal annealing can significantly reduce the amount of oxygen vacancies defects as evidenced by X-ray photoelectron spectroscopy spectra due to the in-diffusion of oxygen from air to the films. As shown by X-ray diffraction, the annealing repairs the crystalline structure and releases the stress. The absorption coefficient of the films increases with the annealing temperature due to the increased density. The annealing temperature reaching 600 °C leads to relatively significant changes in grain size and band gap. From the results of band gap and Hall-effect measurements, the annealing temperature lower than 600 °C reduces the oxygen vacancies defects acting as shallow donors, while it is suspected that the annealing temperature higher than 600 °C can further remove the oxygen defects introduced mid-gap states.

Tantalum (Ta)-doped titanium oxide (TiO₂) thin films are grown by plasma enhanced atomic layer deposition (PEALD), and used as both an electron transport layer and hole blocking compact layer of perovskite solar cells. The metal precursors of tantalum ethoxide and titanium isopropoxide are simultaneously injected into the deposition chamber. The Ta content is controlled by the temperature of the metal precursors. The experimental results show that the Ta incorporation introduces oxygen vacancies defects, accompanied by the reduced crystallinity and optical band gap. The PEALD Ta-doped films show a resistivity three orders of magnitude lower than undoped TiO₂, even at a low Ta content (0.8–0.95 at.%). The ultraviolet photoelectron spectroscopy spectra reveal that Ta incorporation leads to a down shift of valance band and conduction positions, and this is helpful for the applications involving band alignment engineering. Finally, the perovskite solar cell with Ta-doped TiO₂ electron transport layer demonstrates significantly improved fill factor and conversion efficiency as compared to that with the undoped TiO₂ layer.

Hafnium oxide (HfO₂) thin film has remarkable physical and chemical properties, which makes it useful for a variety of applications. In this work, HfO₂ films were prepared on silicon through plasma enhanced atomic layer deposition (PEALD) at various substrate temperatures. The growth per cycle, structural, morphology and crystalline properties of HfO₂ films were measured by spectroscopic ellipsometer, grazing-incidence X-ray diffraction (GIXRD), X-ray reflectivity (XRR), field-emission scanning electron microscopy, atomic force microscopy and x-ray photoelectron spectroscopy. The substrate temperature dependent electrical properties of PEALD–HfO₂ films were obtained by capacitance–voltage and current–voltage measurements. GIXRD patterns and XRR investigations show that increasing the substrate temperature improved the crystallinity and density of HfO₂ films. The crystallinity of HfO₂ films has a major effect on electrical properties of the films. HfO₂ thin film deposited at 300 °C possesses the highest dielectric constant and breakdown electric field.

Amorphous Gallium oxide (Ga₂O₃) thin films were grown by plasma-enhanced atomic layer deposition using O₂ plasma as reactant and trimethylgallium as a gallium source. The growth rate of the Ga₂O₃ films was about 0.6 Å/cycle and was acquired at a temperature ranging from 80 to 250 °C. The investigation of transmittance and the adsorption edge of Ga₂O₃ films prepared on sapphire substrates showed that the band gap energy gradually decreases from 5.04 to 4.76 eV with the increasing temperature. X-ray photoelectron spectroscopy (XPS) analysis indicated that all the Ga₂O₃ thin films showed a good stoichiometric ratio, and the atomic ratio of Ga/O was close to 0.7. According to XPS analysis, the proportion of Ga³⁺ and lattice oxygen increases with the increase in temperature resulting in denser films. By analyzing the film density from X-ray reflectivity and by a refractive index curve, it was found that the higher temperature, the denser the film. Atomic force microscopic analysis showed that the surface roughness values increased from 0.091 to 0.187 nm with the increasing substrate temperature. X-ray diffraction and transmission electron microscopy investigation showed that Ga₂O₃ films grown at temperatures from 80 to 200 °C were amorphous, and the Ga₂O₃ film grown at 250 °C was slightly crystalline with some nanocrystalline structures.

Zinc oxide (ZnO) attracts much attention owing to its remarkable electrical and optical properties for applications in optoelectronics. In this study, ZnO thin films were prepared by spatial atomic layer deposition with diethylzinc and water as precursors. The substrate temperature was varied from 55 to 135 °C to investigate the effects on the optical, electrical, and structural properties of the films. All ZnO samples exhibit an average transmittance in visible and near-infrared light range exceeding 80% and a resistivity in the range of (3.2–9.0) × 10⁻³ Ω·cm when deposited on a borosilicate glass with a refractive index of ≈1.52. The transmittance, band gap, refractive index, and extinction coefficient are rarely affected, while the resistivity only slightly decreases with increasing temperature. This technique provides a wide process window for depositing ZnO thin films. The results revealed that the films deposited at a substrate of 55 °C were highly crystalline with a preferential (1 0 0) orientation. In addition, the grains grow larger as the substrate temperature increases. The electrical properties and reliability of ZnO/PET samples are also studied in this paper.

Recombination of charge carriers at silicon surfaces is one of the biggest loss mechanisms in crystalline silicon (c-Si) solar cells. Hafnium oxide (HfO₂) has attracted much attention as a passivation layer for n-type c-Si because of its positive fixed charges and thermal stability. In this study, HfO₂ films are deposited on n-type c-Si using remote plasma atomic layer deposition (RP-ALD). Post-annealing is performed using a rapid thermal processing system at different temperatures in nitrogen ambient for 10 min. The effects of post-annealing temperature on the passivation properties of the HfO₂ films on c-Si are investigated. Personal computer one dimension numerical simulation for the passivated emitter and rear contact (PERC) solar cells with the HfO₂ passivation layer is also presented. By means of modeling and numerical computer simulation, the influence of different front surface recombination velocity (SRV) and rear SRV on n-type silicon solar cell performance was investigated. Simulation results show that the n-type PERC solar cell with HfO₂ single layer can have a conversion efficiency of 22.1%. The PERC using silicon nitride/HfO₂ stacked passivation layer can further increase efficiency to 23.02% with an open-circuit voltage of 689 mV.