Phonetics plays a major role in the fabrication of prostheses. This study aimed to assess the knowledge of students regarding the role of phonetics in denture fabrication and to improve the educational process and the clinical application. The study was conducted at the College of Dentistry, Imam Abdulrahman Bin Faisal University, and involved a survey of 344 dental students and interns. The questionnaire contained 20 questions and was divided into three sections: general knowledge, clinical correlations, and clinical evaluations. The data were collected and analyzed statistically using independent t-tests, one-way ANOVA, and Tukey’s post hoc tests. The response rate was 100%. Male and female students only differed significantly in terms of their scores for answers to general knowledge questions, with females achieving better results (p = 0.023). General knowledge varied significantly between fourth-year students and all other levels (p < 0.001), and fifth-year students and interns (p = 0.027). The clinical correlations varied significantly between fourth-year students and interns (p = 0.01), whereas the clinical evaluations varied between all the academic years and interns (fourth-year, p < 0.001; fifth-year, p = 0.003; and sixth-year, p = 0.017). The interns obtained the highest scores in all sections. There was a lack of awareness among dental students of some aspects of the role of phonetics in denture fabrication. The study highlights the deficiencies that need to be addressed and the need for adjustments to the curriculum related to removable prosthodontics in order to improve the knowledge of students regarding the role of speech in denture fabrication.

Background: Candida albicans adhesion to denture base materials is a primary contributor to denture stomatitis. To address this issue, numerous studies have explored the incorporation of various additives into denture base resins to enhance their antifungal properties. Titanium tetrafluoride (TiF₄) is an inorganic fluoride compound that has proven antimicrobial properties but has not yet been tested with denture materials. This study aimed to evaluate the effect of TiF₄ addition into different denture base materials on antifungal activity, surface roughness, hardness, and color properties. Methodology: A total of 200 disc-shaped specimens were prepared—100 heat-polymerized acrylic resins and 100 3D-printed NextDent resins. Four different concentrations of TiF₄ were incorporated: 1 wt%, 2 wt%, 3 wt%, and 4 wt% for both resins, while one group of each resin remained unmodified as a control. All specimens were subjected to thermal cycling for 5000 cycles, and four tests were conducted: Candida albicans adherence, surface roughness, hardness, and color change. A scanning electron microscope (SEM) was used to prove Candida albicans colonies’ adhesion on the specimens’ surfaces, and Fourier-transformed infrared (FTIR) analysis was performed to show the presence of TiF₄ in the resin material; data were analyzed using one-way ANOVA followed by a post hoc test (α = 0.05). Results: TiF₄ significantly reduced the Candida albicans adhesion to heat-polymerized specimens (p < 0.001). Compared to the control group, the incorporation of TiF₄ resulted in a substantial reduction in C. albicans colony counts, with reductions of approximately 97.6% in 1HP, 97.2% in 2HP, 97.4% in 3HP, and complete inhibition (100%) in 4HP. However, there was no significant difference between the 3D-printed ones (p = 0.913). Surface roughness, hardness, and color change of heat-polymerized groups were not significantly affected by TiF₄ (p > 0.05) except the color of the group treated with 4% (p < 0.05). For the 3D-printed groups, no significant differences were detected between the groups regarding candida count, hardness was significantly increased at 2% TiF₄ compared to the control (p = 0.002), and roughness was least with 4% TiF₄, while the color varied significantly between the groups (p < 0.001). Conclusions: TiF₄ addition decreased Candida albicans adhesion to heat-polymerized denture base materials but showed no antifungal effect on the 3D-printed resin. While roughness remained low in 3D-printed groups at higher concentrations. Hardness was not significantly altered in the heat-polymerized resin, whereas it increased significantly in the modified 3D-printed resin. Color stability was compromised at higher TiF₄ concentrations, particularly in the 3D-printed groups. The type of denture base material and TiF₄ concentration both influenced antifungal activity and denture surface properties.