Sawdust, a cheap by-product of the timber and forestry industry, was considered as a framework structure to prepare superabsorbent polymer with acrylic acid (AA) and acrylamide (AM), the synthetic monomers. The effects of initiator content, crosslinker content, AA content, AM content, degree of neutralization of AA, and reaction temperature on the swelling rate of superabsorbent polymer were investigated. The synthesized polymer was characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM), and thermogravimetric analysis (TGA). Under optimal synthesis conditions, the results showed that the swelling rate of the polymer in deionized water and 0.9% NaCl solution reached 738.12 and 90.18 g/g, respectively. The polymer exhibits excellent swelling ability, thermal stability, and reusability. After the polymer was introduced into the samples (soil or coal), the water evaporation rate of the samples was significantly reduced, and the saturated water holding capacity and pore structure were also significantly improved.

The intrinsic flammability of wood restricts its application in various fields. In this study, we constructed a phytic acid (PA)–silica hybrid system in wood by a vacuum-pressure impregnation process to improve its flame retardancy and smoke suppression. The system was derived from a simple mixture of PA and silica sol. Fourier transform infrared spectroscopy (FTIR) indicated an incorporation of the PA molecules into the silica network. Thermogravimetric (TG) analysis showed that the system greatly enhanced the char yield of wood from 1.5% to 32.1% (in air) and the thermal degradation rates were decreased. The limiting oxygen index (LOI) of the PA/silica-nanosol-treated wood was 47.3%. Cone calorimetry test (CCT) was conducted, which revealed large reductions in the heat release rate and smoke production rate. The appearance of the second heat release peak was delayed, indicating the enhanced thermal stability of the char residue. The mechanism underlying flame retardancy was analyzed by field-emission scanning electron microscope coupled with energy-dispersive spectroscopy (SEM-EDS), FTIR, and TG-FTIR. The improved flame retardancy and smoke-suppression property of the wood are mainly attributed to the formation of an intact and coherent char residue with crosslinked structures, which can protect against the transfer of heat and mass (flammable gases, smoke) during burning. Moreover, the hybrid system did not significantly alter the mechanical properties of wood, such as compressive strength and hardness. This approach can be extended to fabricate other phosphorus and silicon materials for enhancing the fire safety of wood.

The synergistic effect of hierarchically porous zeolites on the fire retardancy and fire toxicity of ammonium polyphosphate (APP) treated wood composites was studied in this work. Hierarchically porous 4A (H4A) zeolite and 4A zeolite were hydrothermally synthesized and characterized. Several groups of wood composites containing APP as fire retardant and H4A/4A zeolites as synergists were fabricated. Thermogravimetric (TG) results showed that H4A zeolite increased the char formation and enhanced the thermal stability of APP treated wood at higher temperature. Cone calorimetry test results suggested that H4A zeolite reduced the heat release rate (HRR) and decreased CO produce rate (COPR) of APP treated wood composites. Moreover, H4A also exhibited better smoke suppression than 4A zeolite when the APP content was small. These results demonstrated that H4A zeolites may be a promising synergistic component for improving the fire retardancy and reducing the fire toxicity of APP treated wood composites.