The incorporation of circulating fluidized bed (CFB) fly ash into self-leveling cement-based (SLC) paste production presents significant environmental advantages. However, its addition deteriorates the fresh properties of the paste, posing challenges for practical implementation. This research examined the fresh properties of SLC paste blended with CFB fly ash, emphasizing fluidity, rheological characteristics, and bleeding rate. To enhance flowability, polycarboxylate superplasticizer (PCE) was incorporated, with particular emphasis on its interaction with CFB fly ash. The findings reveal that adding CFB fly ash to cement-based paste significantly decreased fluidity while increasing yield stress and plastic viscosity. Incorporating 20 wt.% CFB fly ash reduced paste fluidity by 51.4%, while plastic viscosity and yield stress increased by factors of 2.3 and 73, respectively. While PCE enhanced the fluidity of the blended paste, its water-reducing efficiency diminished, and the bleeding rate of the paste increased with higher CFB fly ash dosage. The water-reducing capability of PCE in the CFB fly ash-blended cement paste with 20 wt.% CFB fly ash decreased by 40.0%, and the bleeding rate of the paste increased from 0.6% to 6.7%. This effect was primarily attributed to the poor compatibility between PCE and CFB fly ash. The decline in PCE efficiency with higher CFB fly ash content, along with its lower adsorption capacity on CFB fly ash compared to cement particles, further confirmed this incompatibility.

Utilizing waste red-clay brick powder (WRCBP) as a precursor for manufacturing geopolymers is increasingly popular due to its environmental and economic benefits. However, the geopolymerization of this waste remains insufficiently explored. This study evaluates the differences in physical–mechanical properties and microstructural evolution of WRCBP- and fly ash (FA)-based geopolymers to determine the reactivity of WRCBP. Mineral admixtures, including granulated blast furnace slag (GF) and metakaolin (MT), were incorporated with WRCBP to fabricate geopolymer pastes, while FA was used in parallel for comparison. The effects of activator modulus (1.2 and 1.4 for Na₂SiO₃) and curing conditions (65 °C and 90 °C) on the mechanical and microstructural performance of the prepared pastes were investigated through water demand analysis, compressive strength testing, mercury intrusion porosimetry (MIP), and scanning electron microscopy (SEM). The results indicate that WRCBP-based pastes achieved a comparable compressive strength (39.8 MPa) under appropriate alkali-activated and curing conditions relative to FA-based pastes (42.5 MPa). The modulus of the alkaline activator exerted a greater influence on strength development than the raw material composition. For both WRCBP- and FA-based pastes, 65 °C was identified as a more suitable curing temperature. Moreover, compared with FA-based pastes, pastes produced using WRCBP provide enhanced social and economic benefits. Overall, this study confirms that high-performance binders can be engineered by incorporating WRCBP, thereby supporting the development of sustainable low-carbon construction materials.

Inorganic soil stabilizer represents a promising option to tackle the issues that arise from the land-filling of engineering waste spoil (EWS) due to its economic and environmental benefits. This paper investigates the mechanical and microscopic properties of magnesium oxysulfate soil stabilizer (MOSS) pastes. In addition, the mechanical properties of a novel type of engineering waste spoil-based specimens (EWSS), fabricated using MOSS to solidify high-content EWS, were systematically investigated. The results show that a larger mean particle size and BJH adsorption average pore diameter of LBM were found to accelerate the heat flow rate of the hydration reaction. Specifically, the peak heat flow and total hydration heat attained 30.25 mW/g and 283.9 J/g, respectively, under the condition of an MgO-to-MgSO₄ molar ratio of 9: 1 with LBM2 as the raw material. Furthermore, when the weight ratio of EWS rose from 5% to 80%, the compressive and flexural strengths of EWSS pastes at the 28-day curing age were reduced by 47.0% and 53.3% relative to the reference MOSS pastes.