High-temperature-resistant epoxy composites play a crucial role in enhancing the operational reliability and service life of devices such as DC bushings, which is of great significance for the long-term stable operation of ultra-high voltage and flexible power transmission and distribution systems. In this study, the epoxy composite was prepared, and long-term thermal aging tests were conducted at 250 °C and 270 °C. The changes in physical properties, electrical characteristics, and bending strength of epoxy composite were systematically investigated, and the thermal aging mechanism of these materials was elucidated. The experimental results revealed that with the progression of thermal aging, the epoxy composites exhibited volume shrinkage due to the breaking of chemical bonds. After 10 thermal aging cycles at 270 °C, the mass loss rate of the epoxy composite reached 20.52%. At 250 °C, the breakdown strength decreased by 9.9% compared to the unaged state. After aging at 250 °C and 270 °C, the volume resistivity decreased by a maximum of 53.75% and 76.94%, respectively, while the dielectric constant decreased by a maximum of 50.34% and 41.94%, respectively. After 10 aging cycles at 250 °C and 270 °C, the bending strength of the cured epoxy composite decreased by 39.79% and 53.91%, respectively. These findings provide valuable insights into the thermal aging characteristics of epoxy composites used in DC bushings and other electrical devices, offering a scientific basis for material selection and reliability assessment in high-voltage insulation applications.

In this paper, a physical model is established for the finite element calculation of a 770 MVA large hydro generator, considering such complex factors as core saturation, rotor motion, damping winding, and eddy current loss of the damping winding. Through the simulation of three-phase (A, B, C) sudden short circuit and other transient processes with damping windings, the model verification shows that the error between the simulation results of no-load tests and the actual data is less than 5% (no-load maximum 3.87%, short-circuit maximum 4.89%); the deviation between the rated load torque simulation value of 54.29 MN•m and the theoretical value is only 6.8%, and the magnetic density of 0.946T meets the design expectation. The finite element physical calculation model significantly improves the accuracy and engineering applicability of electromagnetic characteristics analysis of large hydro generators.

Cold-spray additive manufacturing (CSAM) is an emerging solid-state deposition technology that effectively mitigates common defects associated with conventional thermal processes, such as oxidation, phase transformation, and residual stresses. In this study, copper–titanium (Cu-Ti) composite coatings were fabricated via high-pressure CSAM using mixed powders with Ti contents of 3, 6, and 10 wt.%. The influence of Ti content and post-heat treatment (350–400 °C) on the tensile properties of the composites was systematically investigated. The results indicate that the ultimate tensile strength (UTS) remained consistently within the range of 265–285 MPa under all conditions, showing only a mild positive correlation with Ti content. In contrast, ductility was significantly influenced by Ti addition, with elongation decreasing markedly as the Ti content increased. Notably, the composite with 3 wt.% Ti heat-treated at 400 °C exhibited a well-balanced combination of tensile strength (270 MPa) and ductility (20% elongation). These findings demonstrate that CSAM-fabricated Cu-Ti composites possess attractive mechanical properties, which can be tailored through Ti content and heat treatment.