Nowadays, the concept of high entropy alloys (HEAs) has expanded the limits of metallurgy and high-quality metallurgical HEAs ingots have already been successfully obtained on an industrial scale. High Chromium Cast Irons (HCCI) and Multi-Component Cast Irons (MCCI) are known to be a useful material for applications when abrasion resistance is required. Inspired by the concepts of high-entropy alloys, a base HCCI was modified, by adding other carbide-forming elements, at concentrations higher than what is currently used, in order to develop a new class of white cast iron, High Entropy White Cast Iron (HEWCI). The characterization of carbides precipitated during the HEWCI solidification was performed by scanning electron microscopy, energy dispersive spectroscopy, electron backscattered diffraction (SEM/EDS/EBSD) and X-ray diffraction (XRD). With the characterization techniques employed, the as-cast microstructure obtained of HEWCI is composed of approximately 50% of austenite matrix and 50% of different types of carbides, MC, M7C3 and M2C carbides.

In this study, the thermophysical properties of low‐sulfur manganese–boron steel with varying boron and sulfur contents at different temperatures are investigated. Density and surface tension are measured between 1550 and 1650 °C using the maximum bubble pressure method, while viscosity is examined between 1530 and 1570 °C using an improved oscillating crucible viscometer. The methods yield results with low error, consistent with existing literature. The density of the base steel decreases from 7057 ± 25 kg m⁻³ at 1550 °C to 6843 ± 85 kg m⁻³ at 1650 °C. The addition of boron (up to 57 ppm) and sulfur (up to 130 ppm) does not significantly change the density. Sulfur, increasing from 39 to 130 ppm, reduces the surface tension from 1416 ± 12 to 1302 ± 9 mN m⁻¹ at 1650 °C. Boron's effect on surface tension varies, possibly influenced by other elements like oxygen. Viscosity ranges from 5.74 to 6.44 mPa s, with boron and sulfur additions causing minimal changes, the largest deviation being 8%. In these results, valuable data for the simulation, modeling, control, and optimization of liquid steel processing are provided.

Density, surface tension, and viscosity of various liquid electrical steels are measured at different temperatures, varying in their silicon content between 3 and 6 mass%. Density and surface tension are determined using the maximum bubble pressure method, while viscosity is investigated comparatively using a vibrating finger viscometer and an oscillating crucible viscometer. The results are compared with models known from the literature. Based on this, the density of the steel [ρ] = kg m⁻³ and the surface tension [σ] = N m⁻¹ can be described as a function of temperature [θ] = °C and silicon content [Si] = mass% using the equations: , . There is a lack of experimental data in the literature for high‐temperature thermophysical properties for electrical steels. This underlines once again the novelty and significance of this study, as the determined thermophysical properties are essential for a wide range of applications. For instance, they are crucial in the production of metallic powders for additive manufacturing by atomization to adjust the properties of the powders precisely. The findings are also important for steelmaking itself, as the corrosion behavior of refractory material can be better determined.

To obtain a successful product during additive manufacturing, the powder as a raw material must have the high quality. The purpose of this work is to investigate CrMnNi steel powders obtained by inert gas atomization with nickel content: 3, 6, and 9 wt% and to identify dependencies between the powder size and morphology, solidification structure, and change in chemical composition and thermophysical properties. Particle size distribution is measured by a laser scattering analyzer: d₅₀ value are 82.02, 69.32, and 75.54 μm for powders with 3, 6, and 9 wt%, respectively. Surface tension (ST) measurements are made by maximum bubble pressure method: for steels with 3, 6, and 9 wt% at temperature 1500 °C, ST is 1.01, 1.07, and 1.15 mN m⁻¹, respectively. It is found that the change in particle size affects the chemical composition, the content of the ferromagnetic phase and secondary dendritic arm‐spacing. Changes in the content of elements such as S, O, N, and Mn are determined, depending on the diameter of the particles. The influence of changes in content of S, O, and N on the thermophysical properties such as ST is investigated.

This study explores the thermophysical properties and crystallization behavior of two industrial Mold Fluxes (MF1 and MF2) used in continuous steel casting. Viscosity, density, and surface tension were measured using the Rotating Bob Viscometry (RBV) and the Maximum Bubble Pressure (MBP) method, while crystallization dynamics were assessed via the Single Hot Thermocouple Technique (SHTT). Both fluxes showed temperature-dependent viscosity with distinct break temperatures influenced by chemical composition. MF1 had higher viscosity and activation energy (127.72 kJ mol⁻¹) than MF2 (112.11 kJ mol⁻¹) due to its higher Al₂O₃ content. Density and surface tension decreased linearly from 1523 to 1623 K, with values of 2642–2618 kg m⁻³ and 299–291 mN m⁻¹ for MF1, and 2708–2656 kg m⁻³ and 348–305 mN m⁻¹ for MF2. Crystallization analysis showed that MF1 required higher cooling rates (critical cooling rates: 21 K s⁻¹ vs. 18 K s⁻¹ for MF2) for glass formation, highlighting its greater glass-former content.