Cu₂V₂O₇/Cu₃V₂O₈/g-C₃N₄ heterojunctions (CVCs) were prepared successfully by the reheating synthesis method. The thermal etching process increased the specific surface area. The formation of heterojunctions enhanced the visible light absorption and improved the separation efficiency of photoinduced charge carriers. Therefore, CVCs exhibited superior adsorption capacity and photocatalytic performance in comparison with pristine g-C₃N₄ (CN). CVC-2 (containing 2 wt% of Cu₂V₂O₇/Cu₃V₂O₈) possessed the best synergistic removal efficiency for removal of dyes and antibiotics, in which 96.2% of methylene blue (MB), 97.3% of rhodamine B (RhB), 83.0% of ciprofloxacin (CIP), 86.0% of tetracycline (TC) and 80.5% of oxytetracycline (OTC) were eliminated by the adsorption and photocatalysis synergistic effect under visible light irradiation. The pseudo first order rate constants of MB and RhB photocatalytic degradation on CVC-2 were 3 times and 10 times that of pristine CN. For photocatalytic degradation of CIP, TC and OTC, it was 3.6, 1.8 and 6.1 times that of CN. DRS, XPS VB and ESR results suggested that CVCs had the characteristics of a Z-scheme photocatalytic system. This study provides a reliable reference for the treatment of real wastewater by the adsorption and photocatalysis synergistic process.

NiS cocatalyst modified LaFeO ₃ /g-C ₃ N ₄ heterostructures were prepared and their enhanced photocatalytic hydrogen evolution performance under visible light irradiation was presented.

Mesoporous LaFeO₃/g-C₃N₄ Z-scheme heterojunctions (LFC) were synthesized via the incorporation of LaFeO₃ nanoparticles and porous g-C₃N₄ ultrathin nanosheets. The as prepared LFC were characterized by transmission electron microscopy, scanning electron microscopy, atomic force microscopy, X-ray photoelectron spectroscopy, powder X-ray diffraction, Raman spectra and N₂ adsorption analysis. The structural analysis indicated that the reheating process and the addition of NH₄Cl in the thermal polymerization were the key factors to get porous g-C₃N₄ ultrathin nanosheets and to obtain high specific surface areas of LFC. It remarkably enhanced the adsorption capacity and photocatalytic degradation of LFC for removal of oxytetracycline (OTC). The effect of the mass percentage of LaFeO₃ in LFC, pH and temperature on the OTC adsorption was investigated. The LaFeO₃/g-C₃N₄ heterojunction with 2 wt % LaFeO₃ (2-LFC) exhibited highest saturated adsorption capacity (101.67 mg g⁻¹) and largest photocatalytic degradation rate constant (1.35 L g⁻¹ min⁻¹), which was about 9 and 5 times higher than that of bulk g-C₃N₄ (CN), respectively. This work provided a facile method to prepare mesoporous LaFeO₃/g-C₃N₄ heterojunctions with especially well adsorption and photocatalytic activities for OTC, which can facilitate its practical applications in pollution control.

In this study, we first manufactured ultrathin g-C₃N₄ (CN) nanosheets by thermal etching and ultrasonic techniques. Then, EuVO₄ (EV) nanoparticles were loaded onto CN nanosheets to form EuVO₄/g-C₃N₄ heterojunctions (EVCs). The ultrathin and porous structure of the EVCs increased the specific surface area and reaction active sites. The formation of the heterostructure extended visible light absorption and accelerated the separation of charge carriers. These two factors were advantageous to promote the synergistic effect of adsorption and photocatalysis, and ultimately enhanced the adsorption capability and photocatalytic removal efficiency of methylene blue (MB). EVC-2 (2 wt% of EV) exhibited the highest adsorption and photocatalytic performance. Almost 100% of MB was eliminated via the adsorption–photocatalysis synergistic process over EVC-2. The MB adsorption capability of EVC-2 was 6.2 times that of CN, and the zero-orderreaction rate constant was 5 times that of CN. The MB adsorption on EVC-2 followed the pseudo second-order kinetics model and the adsorption isotherm data complied with the Langmuir isotherm model. The photocatalytic degradation data of MB on EVC-2 obeyed the zero-order kinetics equation in 0–10 min and abided by the first-order kinetics equation for10–30 min. This study provided a promising EVC heterojunctions with superior synergetic effect of adsorption and photocatalysis for the potential application in wastewater treatment.

Photocatalytic technology has been recently conducted to remove microbial contamination due to its unique features of nontoxic by-products, low cost, negligible microbial resistance and broad-spectrum elimination capacity. Herein, a novel two dimensional (2D) g-C₃N₄/Bi(OH)₃ (CNB) heterojunction was fabricated byincorporating Bi(OH)₃ (BOH) nanoparticles with g-C₃N₄ (CN) nanosheets. This CNB heterojunction exhibited high photocatalytic antibacterial efficiency (99.3%) against Escherichia coli (E. coli) under visible light irradiation, which was 4.3 and 3.4 times that of BOH (23.0%) and CN (28.0%), respectively. The increase in specific surface area, ultra-thin layered structure, construction of a heterojunction and enhancement of visible light absorption were conducive to facilitating the separation and transfer of photoinduced charge carriers. Live/dead cell staining, sodium dodecyl sulfate-polyacrylamide gel electrophoresis (SDS-PAGE) assays and scanning electron microscopy (SEM) have been implemented to investigate the damage to the cell membrane and the leakage of the intracellular protein in the photocatalytic antibacterial process. The e⁻, h⁺ and O₂^•− were the active species involved in this process. This study proposed an appropriate photocatalyst for efficient treatment of bacterial contamination.

Black phosphorus (BP) is a novel two-dimensional (2D) material with remarkable potential for use in environmental remediation and energy conversion. However, the practical application of BP is significantly limited by its low catalytic efficiency and poor structural stability. In this study, a Z-scheme BP/BiOBr 2D/2D heterojunction was fabricated using a simple solution reaction method at room temperature. The BP/BiOBr heterojunction exhibited significantly enhanced photocatalytic performance in the degradation of various organic pollutants and the production of hydrogen under visible light irradiation. This improved activity can be attributed to the efficient separation of photogenerated charges and the extended lifetime of charge carriers within the heterojunction. The durability and structural stability of the BiP-10 heterojunction were demonstrated through cycling tests, which maintained high photocatalytic efficiency over multiple uses. This study presents a promising approach to the development of BP-based photocatalytic materials for sustainable environmental and energy applications.