The energy crisis and environmental issues are becoming more severe due to the long-term consumption of fossil fuels. Therefore, novel energy-conversion devices with high energy density and environmental friendliness are expected to provide reliable alternatives to traditional fossil-based energy systems. However, because of the inevitable use of costly precious metals as the electrode catalysts for such devices, their popularization is seriously hindered. Transition metal nitrides (TMNs) exhibit similar surface and adsorption properties to noble metals because the atomic distance between metal atoms increases and the d-band center of metal atoms downshifts after nitrogen atoms enter the metal lattice. TMNs have become one of the best electrode materials to replace noble metal-based electrocatalysts in next-generation energy-storage and energy-conversion devices. In this review, the recent developments in the electrocatalytic application of TMNs are covered. First, we discuss the structure and activity origin of TMNs and introduce the common synthesis methods for the preparation of TMNs. Subsequently, we illustrate the applications of mono-metallic TMNs and multi-metallic TMNs in oxygen-reduction reaction, oxygen-evolution reaction, and bifunctional oxygen reduction and evolution reactions. Finally, we summarize the challenges of TMNs encountered at the present stage, and expect their future development.

Electrochemical water splitting has wide applicability in preparing high-density green energy. The Proton exchange membrane (PEM) water electrolysis system is a promising technique for the generation of hydrogen due to its high electrolytic efficiency, safety and reliability, compactness, and quick response to renewable energy sources. However, the instability of catalysts for electrochemical water splitting under operating conditions limits their practical applications. Until now, only precious metal-based materials have met the requirements for rigorous long-term stability and high catalytic activity under acid conditions. In this review, the recent progress made in this regard is presented and analyzed to clarify the role of precious metals in the promotion of the electrolytic decomposition of water. Reducing precious metal loading, enhancing catalytic activity, and improving catalytic lifetime are crucial directions for developing a new generation of PEM water electrolysis catalysts. A summary of the synthesis of high-performance catalysts based on precious metals and an analysis of the factors affecting catalytic performance were derived from a recent investigation. Finally, we present the remaining challenges and future perspectives as guidelines for practical use.

Low Pt utilization and intense carbon corrosion of cathode catalysts is a crucial issue for high‐efficiency proton exchange membrane fuel cells due to the highly demanded long‐term durability and less acquisition/application cost. Herein, structurally tunable graphitized mesoporous carbon (GMC) is obtained by direct high‐temperature pyrolysis and in situ‐controlled mesopore formation; the structure‐optimized GMC1300‐1800 exhibits a mesopore size of 7.54 nm and enhanced corrosion resistance. Functionalized GMC1300‐1800 is loaded with small‐sized Pt nanoparticles (NPs) (1.5 nm) uniformly by impregnation method to obtain Pt/GMC1300‐1800 and form an “internal platinum structure” to avoid sulfonic acid groups poisoning as well as ensure O₂/proton accessibility. Hence, the electrochemically active surface area (ECSA) of Pt/GMC1300‐1800 reaches 106.1 m² g⁻¹_Pt, while mass activity and specific activity at 0.9 V are 2.1 and 1.4 times those of commercial Pt/C, respectively. Notably, the ECSA decay is less than 17% for both 30 000 cycles’ accelerated durability tests (ADTs) of Pt attenuation and carbon attenuation. Accordingly, the optimized mesoporous structure of GMC1300‐1800 significantly decreases the coverage of sulfonic acid groups on Pt NPs, leading to the highest peak power density in the single‐cell test. Density functional theory calculations demonstrate the synergistic effect between graphitization and mesoporosity on enhancing the accessibility and durability of the catalysts.

Single-atom catalysts characterized by their novel electronic configurations and exceptional atomic utilization efficiency have emerged as potential alternatives to costly noble metal catalysts, garnering extensive research attention in various electrocatalytic fields. However, the inherent characteristics of single metal centers constrain their further application in catalyzing multi-electron reactions. In contrast, multi-atom catalysts (MACs), particularly dual-atom catalysts (DACs), possess multiple active metal sites that can significantly enhance catalytic performance through synergistic effects. This review summarizes recent developments in multi-atom catalysts, focusing on synthesis methods, design strategies, and the correlation between interatomic synergy and catalytic efficiency. Furthermore, we discuss their applications in key electrochemical reactions, including the hydrogen evolution reaction, oxygen reduction reaction, and oxygen evolution reaction. Finally, we outline the opportunities and challenges in this field to guide the development of high-efficiency catalysts for sustainable energy conversion applications.