In this study, a commercial anion-exchange resin (D301), known for high regenerability but limited selectivity, was chemically modified to enhance its sorption performance. The modification included graft polymerization of glycidyl methacrylate followed by thiourea functionalization, yielding a new sorbent, TD301, with chelating functional groups. Characterization using SEM/EDS, IR spectroscopy, XPS, and zeta potential measurements confirmed the successful introduction of sulfur- and nitrogen-containing groups, increased surface roughness, and decreased surface charge in the pH range 2–6. These changes shifted the sorption mechanism from nonspecific ion exchange to selective coordination. Sorption properties of TD301 were evaluated in mono- and bimetallic Mo–W systems, as well as in solutions obtained from real ore decomposition. The modified sorbent showed fast sorption kinetics and high selectivity for Mo(VI) at pH 1.5, while retaining high W(VI) uptake at pH 0.5. In binary systems, separation factors (α) reached 128.4, greatly exceeding those of unmodified D301. In real leachates (Mo ≈ W ≈ 0.04 g/L), TD301 selectively extracted W at pH 0.66 and Mo at pH 1.5. These findings demonstrate that TD301 is an effective sorbent for pH-dependent Mo/W separation in complex matrices, with potential for resource recovery, wastewater treatment, monitoring, and suitability for repeated use.

Optimized Decomposition Conditions for Tungsten-Molybdenum Ores with Diverse Mineral Compositions are reported.

This article models the adsorption of molybdenum and tungsten on the D301 sorbent and evaluates its suitability for their separation.