In this paper, the impact of mechanical alloying (MA) and spark plasma sintering (SPS) on the phase evolution and mechanical properties development of CoCrFeNiTi high–entropy alloys (HEAs) was investigated. The microstructure and properties of the material were examined, using X-ray diffraction (XRD) for phase identification, scanning electron microscopy (SEM) for surface morphology observation, transmission electron microscopy (TEM) for microstructural analysis, and hardness testing to evaluate mechanical performance. The milled powder exhibited nanocrystalline solid solution microstructure with grain sizes below 48 nm, composed of 83% face–centered cubic (FCC) and 17% body–centered cubic (BCC) phases. Mechanically, the bulk CoCrFeNiTi alloy exhibited exceptional strength attributes, as evidenced by a Vickers hardness value reaching 675 Hv, along with a compressive strength of 1894 MPa and a yield stress of 1238 MPa. These findings suggested that the synergistic effects of mechanical alloying and SPS processing can precisely control the phase stability, microstructure refinement, and property optimization in CoCrFeNiTi HEA, with particular promise for advanced structural applications.