The breakdown property of oil-impregnated paper is a key factor for converter transformer design and operation, but it is not well understood. In this paper, breakdown voltages of oil-impregnated paper were measured at different temperatures. The results showed that with the increase of temperature, electrical, electro-thermal and thermal breakdown occurred successively. An electro-thermal breakdown model was proposed based on the heat equilibrium and space charge transport, and negative differential mobility was introduced to the model. It was shown that carrier mobility determined whether it was electrical or thermal breakdown, and the model can effectively explain the temperature-dependent breakdown.

This study explores the possibility of enhancing both mechanical and breakdown properties of insulating presspaper by the introduction of an organic nano additive. Four different concentrations of nanofibrillated cellulose (NFC) were taken into account: 0.5 wt %, 2.5 wt %, 5 wt %, and 10 wt %. Presspaper containing no NFC was also prepared as a reference. Obtained samples were characterized by scanning electron microscope (SEM), Fourier transform infrared spectroscopy (FTIR), and X-ray diffraction (XRD). Mechanical properties and breakdown behaviors were measured. Results show that the addition of 10 wt % NFC to softwood fibers can achieve the best performance. Tensile strength of reference presspaper is 109 MPa, whereas that of presspaper modified by 10 wt % NFC is 136 MPa, resulting in a 25% increase. The improved tensile strength can be attributed to the increased density and inter fiber bond strength. More importantly, presspaper reinforced by 10 wt % NFC can also achieve enhanced AC and DC breakdown strengths, which are 19% and 21% higher than those of the reference presspaper. It is concluded that NFC is likely to be a promising nano additive for cellulose insulation.

The insulation property at high voltage frequencies has become a tough challenge with the rapid development of high-voltage and high-frequency power electronics. In this paper, the electrical treeing behavior of silicone rubber (SIR) is examined and determined at various voltage frequencies, ranging from 50 Hz to 130 kHz. The results show that the initiation voltage of electrical trees decreased by 27.9% monotonically, and they became denser when the voltage frequency increased. A bubble-shaped deterioration phenomenon was observed when the voltage frequency exceeded 100 kHz. We analyze the typical treeing growth pattern at 50 Hz (including pine-like treeing growth and bush-like treeing growth) and the bubble-growing pattern at 130 kHz. Bubbles grew exponentially within several seconds. Moreover, bubble cavities were detected in electrical tree channels at 50 Hz. Combined with the bubble-growing characteristics at 130 kHz, a potential growing model for electrical trees and bubbles in SIR is proposed to explain the growing patterns at various voltage frequencies.

Nanocellulose-modified presspaper is a promising solution to achieve cellulose insulation with better performance, reducing the risk of electrical insulation failures of a converter transformer. Predicting the dielectric properties will help to further design and improvement of presspaper. In this paper, a multivariable method was adopted to determine the effect of softwood fiber on the macroscopic performance of presspaper. Based on the parameters selected using the optimum subset method, a multiple linear regression was built to model the relationship between the fiber properties and insulating performance of presspaper. The results show that the fiber width and crystallinity had an obvious influence on the mechanical properties of presspaper, and fiber length, fines, lignin, and nanocellulose had a significant impact on the breakdown properties. The proposed models exhibit a prediction accuracy of higher than 90% when verified with the experimental results. Finally, the effect of nanocellulose on the breakdown strength of presspaper was taken into account and new models were derived.

The reactive current can be reduced effectively by decreasing the frequency of the voltage in partial discharge (PD) test, especially for equipment with large capacitance. Thus, the cost and volume of the test power supply can be economized. To figure out the difference of PD characteristics in transformer oil between rated alternating-current (AC) frequency (50 Hz) and low frequency, tests are conducted from rated AC frequency to very low frequency (0.1 Hz) based on impulse current method. The results show that with the decrease of frequency, the inception voltage increases. The maximum and mean magnitude of discharge and pulse repetition rate first increase slightly, then decrease obviously. The main features of the variation of phase resolved PD (PRPD) patterns, discharge statistical patterns (phase distribution of maximum and mean discharge magnitude, pulse repetition rate q_max–φ, q_mean–φ, n–φ; and number distribution of discharge magnitude n–q), and their characteristic parameters (skewness S_k⁺, S_k⁻; kurtosis K_u⁺, K_u⁻; asymmetry A_sy; and correlation coefficient C_c) are depicted in detail, which should be paid attention to when using low frequency voltage. The inner mechanism for these variations is discussed from the aspects of the influence on electric field distribution and discharge process of frequency. Additionally, the variation trend of PD characteristics with the decrease of frequency can provide more information about insulation defect, which can be the supplement for discharge mode recognition.