Owing to superior strength-ductility combination and great potential for applications in extreme conditions, high-entropy alloys (HEAs) with the face-centered cubic (FCC) structure have drawn enormous attention. However, the FCC structure limits yield strength and makes the alloys unable to meet ever-increasing demands for exploring the universe. Here, we report a strategy to obtain FCC materials with outstanding mechanical properties in both ambient and cryogenic environments, via exploiting dynamic development of the interstitial-driven local chemical order (LCO). Dense laths composed of the multiscaled LCO domains evolve from planar-slip bands that form in the prior thermomechanical processing, contributing to ultrahigh yield strengths over a wide temperature range. During cryogenic tensile deformation, LCO further develops and promotes remarkable dislocation cross-slip. Together with the deformation-driven transformation and twinning, these factors lead to satisfactory work hardening. The cryogenic loading–promoted LCO, also revealed by ab initio calculations, opens an avenue for designing advanced cryogenic materials.

The pre-sintered preform (PSP) is an advanced technology for repairing the Ni-based superalloy blade in a turbine. In general, boron is added to the Ni-based superalloys in small quantities (1.0 wt.%) on the microstructure evolution and mechanical properties in Ni-based superalloys for the PSP application is rarely studied. The variety, composition and evolution of the precipitates during solution heat treatment in the alloy with high B content were determined by EBSD, EPMA and SEM. The results indicate that Cr, W and Mo-rich M₅B₃ type borides precipitate from the matrix and its area fraction reaches up to about 8%. The area fraction of boride decreases with the prolonging of solution time and the increase of temperature higher than 1120 °C. The borides nearly disappear after solution treatment at 1160 °C for 2 h. The redissolution of boride and eutectic results in the formation of B-rich area with low incipient melting (about 1189 °C). It can bond metallurgically with the blade under the melting point of the blade, which decreases the precipitation of harmful phases of the blade after PSP repairing. The microhardness within the grain in the PSP work-blank first decreases (lower than 1160 °C) and then increases (higher than 1185 °C) with the increase of solution heat treatment temperature due to the dissolving and precipitation of borides. The tensile strength of the combination of PSP work-blank and Mar-M247 matrix at room temperature after solution treatment is related to the area fraction of boride, incipient melting and the cohesion between PSP work-blank and Mar-M247 matrix.

This study investigated how long-term aging (750 °C and 950 °C) affects the microstructure and room-temperature tensile properties of the Ni-Co-Cr superalloy GH3617. Characterization (SEM, EDS, EBSD) showed that initial aging (750 °C, 500 h) formed discontinuous M₂₃C₆ carbides, pinning grain boundaries and improving strength. Prolonged aging (750 °C, 5000 h) caused M₂₃C₆ to coarsen into brittle chain-like structures (width up to 1.244 μm) and precipitated M₆C carbides, degrading grain boundaries. Aging at 950 °C accelerated this coarsening via LSW kinetics (rate constant: 6.83 × 10⁻² μm³/s), with Mo segregation promoting M₆C formation. Tensile properties resulted from competing γ′ precipitation strengthening (post-aging strength increased up to 23.3%) and grain boundary degradation (elongation dropped from 70.1% to 43.3%). Fracture shifted from purely intergranular (cracks along M₂₃C₆/γ interfaces at 750 °C) to mixed mode (cracks initiated by M₆C fragmentation at 950 °C). These insights support superalloy microstructure optimization and lifetime prediction.