This paper presents an in-situ inspection and experimental investigation on the pore solution pH of concrete cover for the corrosion initiation of rebars under a long-term natural carbonation reaction. A 77-year-old steel mill was inspected, and 35 concrete column cover samples were collected to test the pH of the pore solution and phase compositions layer by layer. The variation in pH and phase compositions of the concrete along the cover depth was studied. The in-situ inspection results indicate that the rebar embedded in concrete had begun to corrode when the carbonation depth was almost less than one-third of the cover depth. The corrosion initiation of rebars embedded in concrete can occur when the pH is between 11.3 and 12.1. The pore solution pH test results and X-ray diffraction (XRD) analysis indicated that there is a semi-carbonated zone between the fully carbonated zone and the rebar. The pH of a fully carbonated zone is in a range of 8.0–9.5, and the pH of a semi-carbonated zone is between 9.5 and 12.1.

This study investigates the effects of basalt–polypropylene fibers on the compressive strength and splitting tensile strength of concrete and calculates the fractal dimension of the pore structure of concrete by using a fractal model based on the optical method. Test results reveal that hybrid fibers can improve the compressive strength and splitting tensile strength of concrete, and the synergistic effect of the hybrid fibers is strongest when the contents of basalt fiber (BF) and polypropylene fiber (PF) are 0.05% each, and that the maximum increments in compressive strength and splitting tensile strength are 5.06% and 9.56%, respectively. The effect of hybrid fibers on splitting tensile strength is greater than on compressive strength. However, hybrid fibers have adverse effects on mechanical properties when the fiber content is too high. The pore structure of basalt–polypropylene fiber-reinforced concrete (BPFRC) exhibits obvious fractal characteristics, and the fractal dimension is calculated to be in the range of 2.297–2.482. The fractal dimension has a strong correlation with the air content and spacing factor: the air content decreases significantly whereas the spacing factor increases with increasing fractal dimension. In addition, the fractal dimension also has a strong positive correlation with compressive strength and splitting tensile strength. Therefore, the fractal dimension of the pore structure can be used to evaluate the microscopic pore structure of concrete and can also reflect the influence of the complexity of the pore structure on the macroscopic mechanical properties of concrete.

The flexural behavior of basalt fiber (BF)/polypropylene fiber (PF)-reinforced concrete (BPRC) was investigated. When the content of BF and PF is 0.1%, the addition of fibers increases the compressive strength of concrete. A BF content of 0.1% has the most obvious effect on improving the compressive strength, but a hybrid fiber content of 0.2% exhibits a negative effect on the compressive strength. The addition of BF and PF can increase the flexural strength and the expansion tortuosity of the fracture cracks, thus enhancing the ductility of concrete. The hybrid fibers with content of 0.1% are most beneficial to increase the flexural strength. However, the ductility of concrete and the tortuosity of fracture crack decrease with the matrix strength, and the improvement proportion of fibers on the flexural strength also decreases. When the BF and PF are mixed, compared to the case of single fiber added, there is no significant change in the damage of BF, whereas the damage of PF is more severe. The flexural toughness index FT_δ effectively characterizes the change in the flexural toughness of BPRC. The hybrid fiber contents of 0.1% and 0.2% exhibit the most significant improving effect on FT-l/600 and FT-l/150, respectively. Considering the influence of fibers on the compressive strength, flexural strength and flexural toughness of concrete, a hybrid content of 0.1% is the optimal choice of fiber content. A prediction model for flexural strength of BPRC is proposed based on the composite material theory.