Copper is a critical material for energy transition and green technologies, making its sustainable use increasingly important. Its superior thermal and electrical conductivity make it highly well-suited for additive manufacturing (AM). In this study, copper sourced from offshore electrical cables was upcycled to produce high-quality metal powder for AM. The scrap was processed to separate the metal from plastic and rubber, then refined through ultrasonic atomization, achieving a purity of ~99.5% wt.% with minimal impurities. Characterization demonstrated good flowability, apparent and tap densities, and a well-distributed particle size. To assess its performance in AM, the powder was printed using Directed Energy Deposition (DED) with a laser beam, confirming its high printability and compatibility with the base material. Finally, a comparative Life Cycle Assessment (LCA) revealed a significant environmental advantage of the recycling-based process over conventional mining, reducing global warming potential by more than 70%. These findings highlight the importance of feedstock origin in AM sustainability and support the adoption of circular economy strategies to lower the environmental footprint of advanced manufacturing.

In the framework of hydrogen production and storage for clean energy generation, the resistance to hydrogen embrittlement of a newly developed austenitic stainless steel is presented. Gas-atomized metal powders prepared from secondary-sourced metals were employed to manufacture test specimens with Laser Powder Bed Fusion (LPBF) technology. After machining and exposure to a controlled, pressurized hydrogen atmosphere at high temperature, the effect of hydrogen charging on the mechanical performance under static and dynamic conditions was investigated. The stabilizing effect of the optimized chemical composition is reflected in the absence of degradation effects on Yield Stress (YS), Ultimate Tensile Stress (UTS), and fatigue life observed for specimens exposed to hydrogen. Moreover, despite a moderate reduction in the elongation at fracture observed by increasing the hydrogen charging time, ductility loss calculated as Relative Reduction of Area (RRA) remains substantially unaffected by the duration of exposure to hydrogen and demonstrates that the austenitic steel is capable of resisting hydrogen embrittlement (HE).