Hybrid materials based on porous organic polymers (POPs) and metal–organic frameworks (MOFs) are increasing attention for advanced separation processes due to the possibility to combine their properties. POPs provide high surface areas, chemical stability, and tunable porosity, while MOFs contribute a high variety of defined crystalline structures and enhanced separation characteristics. The combination (or hybridization) with PIMs gives rise to mixed-matrix membranes (MMMs) with improved permeability, selectivity, and long-term stability. However, interfacial compatibility remains a key limitation, often addressed through polymer functionalization or controlled dispersion of the MOF phase. MOF/COF hybrids are more used as biochemical sensors with elevated sensitivity, catalytic applications, and wastewater remediation. They are also very well known in the gas sorption and separation field, due to their tunable porosity and high electrical conductivity, which also makes them feasible for energy storage applications. Last but not less important, hybrids with other POPs, such as hyper-crosslinked polymers (HCPs), covalent triazine frameworks (CTFs), or conjugated microporous polymers (CMPs), offer enhanced functionality. MOF/HCP hybrids combine ease of synthesis and chemical robustness with tunable porosity. MOF/CTF hybrids provide superior thermal and chemical stability under harsh conditions, while MOF/CMP hybrids introduce π-conjugation for enhanced conductivity and photocatalytic activity. These and other findings confirm the potential of MOF-POP hybrids as next-generation materials for gas separation and carbon capture applications.

Boosting the transport and selectivity properties of membranes based on polymers of intrinsic microporosity (PIMs) toward one specific working analyte of interest is challenging. In this work, a novel family of PIM membranes, prepared by casting and exhibiting optima mechanical properties and high thermal stability, was synthesized from 4,4'-(2,2,2-trifluoro-1-phenylethane-1,1-diyl) bis(benzene-1,2-diol) and two tetrafluoro-nitrile derivatives. Gas permeability measurements evidenced a CO₂/CH₄ selectivity up to 170% relative to the reference polymer, PIM-1, in agreement with their calculated fractional free volume and the analysis of the textural properties by N₂ and CO₂ gas adsorption. Besides, the chemical modification by acid hydrolysis of the PIM membranes favored the permeability for lithium ions (LiCl 2M, 6 × 10^-9 cm²·s^-1) compared to other alkali metal analogs such as sodium (NaCl 2M, 7.38 × 10^-10 cm²·s^-1) and potassium (KCl 2M, 1.05 × 10^-9 cm²·s^-1). Moreover, the complete mitigation of the crossover of redox species with higher molecular sizes than the ions from alkali metal salts was confirmed by using in-line benchtop NMR methods. Additionally, the modified PIM membranes were measured in a symmetric electrochemical flow cell using an aqueous electrolyte by combining lithium ferro/ferricyanide redox compounds and lithium chloride. The electrochemical tests showed low polarization, high-rate capability, and capacity retention values of 99% when cycled at 10 mA·cm^-2 for over 50 cycles. Based on these results, these polymers could be used as highly selective and conducting membranes in electrodialysis for lithium separation and lithium-based redox flow batteries and as a protective layer in high-energy density lithium metal batteries.

Operando ⁷ Li-NMR reveals and quantifies charge-balancing ion transport through a fluorine-free biphenyl-isatin-based membrane in a symmetric iron-based redox flow cell.