A kind of pollution known as electromagnetic interference (EMI), which results from ubiquitous usage of various electronic communication and military radar equipment, has been receiving increasing attention recently. However, large-area EMI shielding on transparent and/or curved surfaces, including building windows, curved glass wall, and special requirements spaces (SRSs), remains hard to achieve. In this paper, a silver nanofiber (AgNF) based flexible and transparent EMI shielding film was successfully assembled via a room-temperature roll-to-roll production method. For transparent application scenario, AgNF with 89% transmittance in visible range and 1 μm thickness shows ~20 dB shielding efficiency (EMI SE). On the other hand, total shielding (>50 dB) is obtained when the thickness of AgNF increases to 10 μm, while its transmittance in visible range remains higher than 75%. Considering the facile and scale-free production technology, this material can be readily applied in large-scale, transparent, and/or SRSs EMI shielding.

A kind of piezoelectric ink was prepared with Li, Ta, Sb co-doped (K, Na)NbO₃ (KNN) powders. Piezoelectric scaffolds with diameters at micrometer scale were constructed from this ink by using direct ink writing method. According to the micro-morphology and density test, the samples sintered at 1100 °C for 2 h have formed ceramics completely with a high relative density of 98%. X-ray diffraction (XRD) test shows that the main phase of sintered samples is orthogonal (Na_0.52K_0.4425Li_0.0375)(Nb_0.87Sb_0.07Ta_0.06)O₃. The piezoelectric constant d₃₃ of 280 pC/N, dielectric constant ε of 1775, remanent polarization P_r of 18.8 μC/cm² and coercive field E_c of 8.5 kV/cm prove that the sintered samples exhibit good electrical properties. The direct ink writing method allows one to design and rapidly fabricate piezoelectric structures in complex three-dimensional (3D) shapes without the need for any dies or lithographic masks, which will simplify the process of material preparation and offer new ideas for the design and application of piezoelectric devices.

Metamaterials offer a powerful way to manipulate a variety of physical fields ranging from wave fields (electromagnetic field, acoustic field, elastic wave, etc.), static fields (static magnetic field, static electric field) to diffusive fields (thermal field, diffusive mass). However, the relevant reports and studies are usually limited to a single physical field or functionality. In this study, we proposed and experimentally demonstrated a bifunctional metamaterial which could manipulate thermal and electric fields simultaneously and independently. Specifically, a composite with independently controllable thermal and electric conductivity was introduced, on the basis of which a bifunctional device capable of shielding thermal flux and concentrating electric current simultaneously was designed, fabricated and characterized. This work provides an encouraging example of metamaterials transcending their natural limitations, which offers a promising future in building a broad platform for the manipulation of multi-physics fields.