Woody raw materials of wood-based panels like fiberboard and particleboard are one of the primary sources of product odor and one of the indicators affecting the comprehensive health risk assessment of wood-based panel products. This study employed Gas Chromatography-Mass Spectrometry-Olfactometry (GC-MS-O) to investigate the odorant composition and odor characteristics, including Total Odor Concentration (TOC), odor intensity (OI), odor activity value (OAV), and risk value (RV), of 22 wood species commonly used in fiberboard and particleboard production in China. This research identified the major odor-active compounds in wood and provided recommendations for selecting wood raw materials suitable for low-odor fiberboards and particleboards produced by integrating RV and toxicity classification data. The results showed that the main compound types influencing wood odor in 22 wood species were predominantly terpenes, aldehydes, and alcohols. Woods of Cinnamomum, Machilus, and Pinus contained a higher number of dominant odor compounds (OAV > 1 and OI ≥ 3). Wood with stronger odor intensity included Cinnamomum, Pinus, Machilus, Bischofia, and Saurauia. The total RV of Cinnamomum, Pinus, Machilus, Cunninghamia, and Bombax wood exceeded one, necessitating special attention when used as raw materials for wood-based panels. Camphor in Cinnamomum and Machilus wood was the most concentrated odorant, followed by 3-Carene in Pinus wood. Odorants with high OAV included Longifolene, δ-Cadinene, Terpinen-4-ol, 2-Nonenal, γ-Terpinene, d-Limonene, 3-methyl-Butanal, Octanal, α-Pinene, Hexanal, D-Camphor, and trans-Calamenene. Odorants with high RV included terpenes, alcohols, aldehydes, and ketones, such as Camphor, 3-Carene, Eucalyptol, α-Terpineol, β-Pinene, α-Santalene, δ-Cadinene, Safrole, Longifolene, and d-Limonene. Focusing on the reduction and control of these odor-active compounds represents a primary approach to mitigating odors in fiberboard and particleboard products. However, addressing health risks associated with product odors requires additional attention to four specific substances: Safrole, Camphor, Eucalyptol, and α-Terpineol. Although the total RV for the five wood species exceeds one, this does not necessarily mean the final wood-based panel product’s RV exceeds one, as it also depends on the influence of the production process. Therefore, further research should be conducted to investigate the effects of various process parameters in wood-based panel production on the odor compounds present in the final panels. From a comprehensive perspective, considering the overall odor characteristics of wood volatiles, all 18 wood species (Salix, Populus, Rhaphiolepis, Ligustrum, Prunus, Fagus, Pterocarya, Firmiana, Celtis, Cunninghamia, Bombax, Bischofia, Ficus, Saurauia, Eucalyptus, Aleurites, Melia, Bridelia) are suitable for the production of low-odor fiberboards and particleboards.

The development of sustainable wood-based composites has driven increasing interest in formaldehyde-free, low-odor, and recyclable bonding systems. However, achieving high mechanical performance and dimensional stability in high-density fiberboards (HDFs) without synthetic adhesives remains a challenge. Here, we report a two-step strategy combining oxidative pretreatment of wood fibers with supramolecular assembly of tannic acid (TA) and sodium ions (Na⁺) to fabricate low-odor, recyclable HDF. Oxidation generated abundant carboxyl groups on the fiber surface, enabling strong coordination and hydrogen-bonding interactions between TA and Na⁺, which constructed robust inter-fiber supramolecular networks without formaldehyde-based adhesives. The resulting HDF exhibited excellent mechanical properties, with an internal bond strength of 3.1 MPa, a modulus of rupture of 49 MPa, and 24 h water thickness swelling of only 12%. Odor and VOC analysis revealed only trace benzene, demonstrating markedly low odor. Furthermore, the reversible nature of Na⁺-TA interactions allowed efficient fiber separation and recyclability under mild aqueous conditions. This oxidation-assisted supramolecular approach provides a sustainable route for producing high-performance, low-odor, and recyclable fiberboards, offering a viable alternative to conventional polymer-bonded wood composites.

Wood, as the oldest natural polymer composite material on Earth, holds significant importance in the era of carbon neutrality and serves as an irreplaceable core material in the furniture and construction industries. As a primary raw material for furniture, wood-based lignocellulosic boards have drawn increasing consumer attention due to their odor characteristics. In order to achieve the determination of odor compounds in lignocellulose-based panels, this study established a method combining dynamic headspace sampling (DHS), gas chromatography–mass spectrometry (GC–MS), and odor activity value (OAV) analysis. To address the wide concentration range of odor compounds in lignocellulose-based panels, a three-level standard curve was established to meet the detection of odor substances in common lignocellulose-based panels. The favorable conditions for each factor were as follows: sheet-shaped samples, TENAX-TA adsorbent, 20 mL headspace vials, and a split ratio of 25:1. The method demonstrated good linearity within the range of 0.002–15 mg/m³, with recovery rates ranging from 94.74% to 103.44%. The method was applied to analyze commercially available particleboard, fiberboard, and plywood. A total of 33 odor components were detected. The results indicated that aldehyde contributed significantly to the odor of particleboard, acids were the main contributors to the odor of fiberboard, and terpenes dominated the odor of plywood. The established method is suitable for the qualitative and quantitative analysis of odor compounds in lignocellulose-based panels and provides reliable technical support for tracing, identifying, and controlling odors in these materials.

Materials exhibiting a Poisson's ratio of zero have attracted considerable interest due to their unique properties and potential applications in various fields, including aerospace, athletic footwear, and sporting equipment. However, the high costs associated with their structural fabrication and the dependence on synthetic chemical materials for most zero Poisson's ratio materials complicate the preparation processes of current elastic materials, resulting in negative environmental impacts. This study presents a sustainable treatment strategy that utilizes the inherent cellular structure of wood to achieve a zero Poisson's ratio, thereby enhancing its elasticity. By strategically selecting tree species with varying tissue compositions and employing simple chemical and heat treatments, we developed a commercially viable elastic wood material with a zero Poisson's ratio that meets diverse stress rebound requirements. The unique internal structure of the wood not only provides high fatigue resistance-capable of withstanding 5000 cycles of compression at a strain of 40 %-but also ensures excellent resilience and processability. At a deformation level of 60 %, the elastic modulus reaches 90.9 MPa. Additionally, the material retains its elasticity even at extremely low temperatures of -196 °C and demonstrates the ability to endure elevated temperatures following carbonization at 1200 °C. This study demonstrates that wood-based materials with a zero Poisson's ratio exhibit remarkable stability after cyclic compression, presenting a viable pathway for developing superelastic materials suitable for both high- and low-temperature applications.

Analysis of changes in TVOC and VOCs chemical composition or odor characteristics of particleboard before and after decoration treatment with resin-impregnated paper (RIP), polypropylene (PP) film and polyvinyl chloride (PVC) film were studied. The effects of these three decoration treatments on masking or suppressing the release of VOCs and odorants from particleboard were explored. The substances that were covered or suppressed and newly introduced before and after processing were identified to provide a basis for reducing the odor emissions of PVC-, PP- and RIP-decorated particleboard. Taking undecorated particleboard and particleboard treated by three types of decorative materials as research subjects, the air permeability of the three decorative materials was tested using the Gurley Permeability Tester. TVOC emissions from the boards were evaluated using the 1 m³ environmental chamber method. Qualitative and quantitative analyses of the samples were conducted via thermal desorption–gas chromatography–mass spectrometry (TD-GCMS). The contribution of odor substances was determined using odor activity value (OAV). The results indicated that the permeability from high to low was PVC film, PP film and RIP. Compared with undecorated particleboard, the TVOC emissions of RIP-decorated boards decreased by 93%, PP-decorated particleboard by 83% but the TVOC emissions of PVC-decorated particleboard increased by 67%. PP decoration treatment masked or suppressed the release of 20 odor substances but introduced xylene, which can increase potentially the health risks for PP-decorated particleboard. PVC decoration treatment masked or suppressed 19 odor substances, but it introduced 12 new compounds, resulting in an overall increase in TVOC emissions. RIP treatment did not introduce new odor substances. After PP film and RIP treatments, both the variety of VOCs released and the number of key odor-contributing compounds and modifying odorants decreased. In contrast, the number of modifying odorants and potential odorants increased after PVC treatment. VOC emissions were effectively masked or suppressed by three decoration treatments, same as the release of substances contributing to overall odor of particleboard was reduced. Among them, PP and RIP decorative materials demonstrate better effects.