Bioactive coatings on VT1-0 commercially pure titanium were formed by the plasma electrolytic oxidation (PEO). A study of the morphological features of coatings was carried out using scanning electron microscopy. A composition of formed coatings was investigated using energy-dispersive spectroscopy and X-ray diffractometry analysis. It was shown that PEO-coatings have calcium phosphate in their composition, which increases the bioactivity of the surface layer. Electrochemical properties of the samples were studied by potentiondynamic polarization and electrochemical impedance spectroscopy in different physiological media: simulated body fluid and minimum essential medium. The data of electrochemical studies indicate more than 15 times decrease in the corrosion current density for the sample with coating (5.0 × 10⁻⁹ A/cm²) as compared to the bare titanium (7.7 × 10⁻⁸ A/cm²). The formed PEO-layers have elastoplastic properties close to human bone (12–30 GPa) and a lower friction coefficient in comparison with bare metal. The wettability of PEO-layers increased. The contact angle for formed coatings reduced by more than 60° in comparison with bare metal (from 73° for titanium to 8° for PEO-coating). Such an increase in surface hydrophilicity contributes to the greater biocompatibility of the formed coating in comparison with commercially pure titanium. PEO can be prospective as a method for improving titanium surface bioactivity.

In this work, the properties of the coatings formed on the Mg-Mn-Ce alloy by plasma electrolytic oxidation (PEO) in electrolytes containing halloysite nanotubes (HNTs) were investigated. The incorporation of halloysite nanotubes into the PEO coatings improved their mechanical characteristics, increased thickness, and corrosion resistance. The studied layers reduced corrosion current density by more than two times in comparison with the base PEO layer without HNTs (from 1.1 × 10⁻⁷ A/cm² to 4.9 × 10⁻⁸ A/cm²). The presence of halloysite nanotubes and products of their dihydroxylation that were formed under the PEO conditions had a positive impact on the microhardness of the obtained layers (this parameter increased from 4.5 ± 0.4 GPa to 7.3 ± 0.5 GPa). In comparison with the base PEO layer, coatings containing halloysite nanotubes exhibited sustained release and higher adsorption capacity regarding caffeine.

This paper presents a method for the formation of composite-polymer-containing coatings on MA8 Mg alloy by plasma electrolytic oxidation (PEO), followed by the deposition of a fluoropolymer from an aqueous suspension of superdispersed polytetrafluoroethylene. The Scanning Electron Microscope(SEM), Energy Dispersive Spectroscopy(EDS), and X-ray Diffraction(XRD) analyses established morphological features as well as elemental and phase composition of composite coatings. The fact that the pores are filled with a fluoropolymer has been experimentally confirmed. An assessment of the corrosion properties of formed composite coatings revealed a decrease in the corrosion current density by more than four orders of magnitude in comparison with the base PEO layer. The highest resistance to the damaging effects of a corrosive environment, according to the results of long-term exposure tests, was demonstrated by coatings after three treatments with polytetrafluoroethylene. The obtained polymer-containing coatings have antifriction properties, reducing the wear of the coatings by more than 27-fold in comparison with the base PEO layer. It was revealed that composite coatings have superhydrophobic properties: the value of the contact angle reaches 154°, and the hysteresis of the contact angle is less than 10°.

This paper presents the results of an evaluation of anti-icing properties of samples obtained by plasma electrolytic oxidation (PEO) with a subsequent application of superdispersed polytetrafluoroethylene (SPTFE) and polyvinylidenefluoride (PVDF). A combined treatment of the samples with SPTFE and PVDF is also presented. It is revealed that impregnation of a PEO layer with fluoropolymer materials leads to a significant increase in surface relief uniformity. Combined PVDF–SPFTE layers with a ratio of PVDF to SPTFE of 1:4 reveal the best electrochemical characteristics, hydrophobicity and icephobic properties among all of the studied samples. It is shown that the decrease in corrosion current density Ic for PVDF–SPFTE coatings is higher by more than five orders of magnitude in comparison with uncoated aluminum alloy. The contact angle for PVDF–SPFTE coatings attain 160.5°, which allows us to classify the coating as superhydrophobic with promising anti-icing performance. A treatment of a PEO layer with PVDF–SPFTE leads to a decrease in ice adhesion strength by 22.1 times compared to an untreated PEO coating.

In case of using titanium alloys in equipment exposed to aggressive media (for example, sea water), it is necessary to take into account and, first of all, prevent the formation of a galvanic couple of titanium and another metal/alloy, which in most cases leads to the corrosion destruction of the latter. Another significant problem of using titanium is its low wear-resistance and poor tribological characteristics. To impart the necessary properties to titanium and its alloys, a composite coating was formed on the top of titanium. For the coating formation, a combination of the plasma electrolytic treatment and polymer spraying was used. The SEM, EDS and XRD analyses established morphological features, elemental and phase composition of the composite coatings. Contact angles and the wettability parameters of the composite coatings were investigated. An analysis of the data obtained showed that composite coatings have better protective properties than untreated material and base PEO coatings.