Comparison of the lubricating mechanisms of nano-additives (graphene, WS ₂ nanoparticles, and WS ₂ /graphene nanocomposites) was carried out using a simplified polar coordinate method.

In many industrial devices, impact-sliding wear is caused by a variety of complex vibrations between the contacted interfaces. Under actual conditions, impact and sliding motions do not occur in only one direction, and different complex impact-sliding motions exist on the tribology surfaces. In this study, an impact-sliding wear test rig is developed to investigate the wear effect of different complex motions. Using this rig, multi-type impact-sliding wear effects are realized and measured, such as those derived from unidirectional, reciprocating, and multi-mode combination motions. These three types of impact–sliding wear running behavior are tested and the wear damage mechanism is discussed.

The operational safety and reliability of a variable gauge train are affected by the anti-fretting wear performance of the locking mechanism. The main purpose of this study is to optimize the surface treatment process for a locking pin material under actual service conditions to alleviate fretting damage. Based on the two basic principles of surface strengthening and friction reduction, a substrate (AISI 4135 steel) surface was treated by laser quenching (LQ), plasma nitriding (PN), and bonded MoS₂ coating. Systematic fretting wear tests were conducted, and the wear behavior and damage mechanism of various treated surfaces were comprehensively investigated. The results indicate that the wear resistances of the LQ- and PN-treated surfaces were significantly improved, and their main wear mechanisms were abrasive wear, delamination, and oxidation wear. The MoS₂ coating exhibits the lowest friction coefficient and energy dissipation due to its self-lubricating property, but it incurs the highest wear rate and failure in the form of plastic deformation. Furthermore, the rough compound layer with a high hardness on the PN-treated surface is conducive to the formation and maintenance of the third-body contact at the fretting interface, consequently resulting in a significant reduction in wear. An optimal surface treatment process for alleviating fretting damage of the locking pin is recommended via comprehensive evaluation, which provides a reference for the anti-fretting protection of related mechanical components.