In actual service, asphalt pavement is subjected to freeze–thaw cycles and ultraviolet radiation (UV) over the long term, which can easily lead to mixture aging, enhanced brittleness, and structural damage, thereby reducing pavement durability. This study focuses on the influence of freeze–thaw cycles and ultraviolet aging on the performance of recycled asphalt mixtures. Systematic indoor road performance tests were carried out, and a fatigue prediction model was established to explore the comprehensive effects of recycled asphalt pavement (RAP) content, environmental action (ultraviolet radiation + freeze–thaw cycle), and other factors on the performance of recycled asphalt mixtures. The results show that the high-temperature stability of recycled asphalt mixtures decreases with the increase in environmental action days, while higher RAP content contributes to better high-temperature stability. The higher the proportion of old materials, the more significant the environmental impact on the mixture; both the flexural tensile strain and flexural tensile strength decrease with the increase in environmental action time. When the RAP content increased from 30% to 50%, the bending strain continued to decline. With the extension of environmental action days, the decrease in the immersion Marshall residual stability and the freeze–thaw splitting strength became more pronounced. Although the increase in RAP content can improve the forming stability, the residual stability decreases, and the freeze–thaw splitting strength is lower than that before the freeze–thaw. Based on the fatigue test results, a fatigue life prediction model with RAP content and freeze–thaw cycles as independent variables was constructed using the multiple nonlinear regression method. Verification shows that the established prediction model is basically consistent with the change trend of the test data. The research results provide a theoretical basis and optimization strategy for the performance improvement and engineering application of recycled asphalt materials.

This study evaluated the aging resistance of bitumen modified with integrated rubber–plastic thermoplastic elastomers (TPEs). Surface-activated low-Mooney reclaimed rubber was compounded with recycled high-density polyethylene, low-density polyethylene, or polypropylene by twin-screw reactive extrusion using a maleic anhydride-grafted styrenic block copolymer compatibilizer. Reference binders contained styrene–butadiene–styrene (SBS), rubber alone, or individual polyolefins. Aging comprised the rolling thin-film oven test, pressure aging vessel conditioning of oven-aged residues, and ultraviolet exposure. Dynamic shear rheometry, Fourier transform infrared spectroscopy, and atomic force microscopy characterized rheological, chemical, and topographic changes. The largest rutting factor and carbonyl aging indices occurred after sequential oven and pressure aging under the selected conditions. The TPE-modified binders showed lower rutting factor and carbonyl aging indices and smaller relative roughness increases than the SBS reference under each protocol. Among the three TPE formulations, the low-density polyethylene composite had the lowest rutting factor aging indices, whereas the high-density polyethylene composite had the lowest carbonyl aging indices and relative roughness increases after pressure and ultraviolet aging. These findings support the laboratory aging-resistance potential of integrated TPEs, with improved interfacial compatibility providing a plausible explanation. The approach offers a route for the high-value utilization of waste rubber and plastics.

To reveal the long-term anti-aging mechanisms of rubber–plastic elastomer-modified asphalt in complex service environments and overcome the inherent defects of single polymer modifiers—namely their susceptibility to degradation or phase separation—this study prepared styrene-butadiene-styrene (SBS), low Mooney rubber (LMMR), and low-density polyethylene (LDPE)-modified asphalts. Simultaneously, an LMMR-LDPE rubber–plastic thermoplastic elastomer (TPE) was fabricated utilizing twin-screw extrusion technology and subsequently used to prepare a composite-modified asphalt. Three aging protocols were simulated: short-term thermo-oxidative aging (RTFOT), long-term pressure aging (PAV), and ultraviolet light aging (UV). A multi-scale quantitative characterization was conducted using a dynamic shear rheometer, Fourier transform infrared spectroscopy, and atomic force microscopy to evaluate the rutting factor, carbonyl index, and surface microroughness of each system before and after aging. The experimental results indicate that the coupled effect of long-term stress and thermal oxidation causes the most severe damage to the colloidal structure of modified asphalt. Conventional SBS-modified asphalt, due to its abundance of unsaturated double bonds, exhibits a sharp increase in the carbonyl index and aging index of the rutting factor after aging, making it highly susceptible to oxidative chain scission. Although LDPE-modified asphalt possesses chemical inertness, it is prone to crystalline phase separation under aging conditions, resulting in a microroughness distortion rate of up to 86.36%. In contrast, the LMMR-LDPE composite system, leveraging the high chemical stability of the saturated aliphatic carbon chain and the flexibility-enhancing and crystallization-inhibiting effects of LMMR, effectively reduces active oxidation sites and improves interfacial compatibility. This composite system exhibits the lowest carbonyl increment and rheological attenuation under all aging conditions, while effectively inhibiting the free migration and agglomeration of macromolecular components. The LMMR-LDPE composite modification technology effectively overcomes the inherent drawbacks of single polymers, such as susceptibility to degradation or segregation, demonstrating excellent long-term macroscopic rheological stability and microscopic phase morphology anti-aging capability. The present findings provide laboratory-scale mechanistic support for the design of durable rubber–plastic-modified asphalt systems, while further pilot-scale, economic, and field validation is still required before practical engineering application can be fully assessed.