Fire-resistant coatings have emerged as crucial materials for reducing fire hazards in various industries, including construction, textiles, electronics, and aerospace. This review provides a comprehensive account of recent advances in fire-resistant coatings, emphasizing environmentally friendly and high-performance systems. Beginning with a classification of traditional halogenated and non-halogenated flame retardants (FRs), this article progresses to cover nitrogen-, phosphorus-, and hybrid-based systems. The synthesis methods, structure–property relationships, and fire suppression mechanisms are critically discussed. A particular focus is placed on bio-based and waterborne formulations that align with green chemistry principles, such as tannic acid (TA), phytic acid (PA), lignin, and deep eutectic solvents (DESs). Furthermore, the integration of nanomaterials and smart functionalities into fire-resistant coatings has demonstrated promising improvements in thermal stability, char formation, and smoke suppression. Applications in real-world contexts, ranging from wood and textiles to electronics and automotive interiors, highlight the commercial relevance of these developments. This review also addresses current challenges such as long-term durability, environmental impacts, and the standardization of performance testing. Ultimately, this article offers a roadmap for developing safer, sustainable, and multifunctional fire-resistant coatings for future materials engineering.

Bio-based polyurethane (PU) coatings offer sustainable alternatives to petrochemical coatings but often suffer from inferior mechanical performance, durability, and chemical resistance. This work addresses that challenge by integrating a trifunctional bio-based crosslinker (glycerol) and a silane-based additive (hexamethyldisilane (HMDS)) to simultaneously enhance structural robustness and hydrophobicity. Coatings were synthesized using a renewable soybean oil polyol (SOP), glycerol (5, 10, 15 and 20 wt.%), and methylene diphenyl diisocyanate (MDI), followed by the addition of HMDS (10, 20, 30, 40 and 50 wt.%). Mechanical tests identified 10 wt.% glycerol as the optimal content, yielding a maximum tensile strength of 47.18 MPa. Incorporating 10 wt.% HMDS into the optimized formulation greatly increased water contact angle (WCA, 95.76°) and chemical resistance with minimal loss of mechanical performance (38.19 MPa, tensile strength); higher HMDS loadings caused network disruption and reduced strength. Calorimetry and thermogravimetric analyses confirmed that the modified coatings retained high thermal stability. This synergistic crosslinker additive strategy produced a structurally robust, water-resistant bio-based coating, demonstrating a viable high-performance sustainable coating solution for industrial applications.