Nowadays, the incorporation of nanoparticles into thermal fluids has become one of the most suitable strategies for developing high-performance fluids. An unconventional improvement of thermo–physical properties was observed with the addition of 1% wt. of nanoparticles in different types of fluids, such as molten salts, allowing for the design of more thermally efficient systems using nanofluids. Despite this, there is a lack of knowledge about the effect that nanoparticles produce on the thermal stability and the decomposition kinetics of the base fluid. The present study performs IR- and UV-vis spectroscopy along with thermogravimetric analysis (TGA) of pure nitrate and nitrate based nanofluids with the presence of SiO₂ and Al₂O₃ nanoparticles (1% wt.). The results obtained support that nanoparticles accelerate the nitrate to nitrite decomposition at temperatures below 500 °C (up to 4%), thus confirming the catalytic role of nanoparticles in nanofluids.

This study presents a groundbreaking exploration into the potential use of refractory tundish deskulling waste (TUN), a magnesium oxide-based by-product from continuous steel casting, as a stabilizing agent for remediating metal and metalloids contaminated soils. Up-flow column horizontal percolation tests were conducted to measure the concentrations of metals and metalloids, pH, and electrical conductivity (EC) in the leachates of two different combinations of contaminated soil and stabilizer (95-5 wt% and 90-10 wt%). The effectiveness of TUN as a soil-stabilizing agent for contaminated soils with metals and metalloids was evaluated by comparing its leachates with those obtained from a sample of a well-established low-grade magnesium oxide (LG-MgO) by-product, which underwent the same testing procedure. The findings revealed a significant correlation between the mobility of the examined metals and metalloids, and the water-soluble or acid phase of the contaminated soil, primarily governed by precipitation-solution reactions. While the stabilizing impact on non-pH-dependent metals, particularly redox-sensitive oxyanions, was less pronounced, both MgO-based stabilizers exhibited a favourable influence on soil pH-dependent metals and metalloids. They achieved this by establishing an optimal pH range of approximately 9.0-10.5, wherein the solubility of metal (hydr)oxides is minimized. Notably, metals like Zn and Cu, which have high leaching potential, experienced a remarkable reduction in leaching - Zn by over 99% and Cu by around 97% - regardless of the stabilizer content. In a broader context, this research champions the principles of the circular economy by offering a technical remedy for treating soils contaminated with pH-dependent metals and metalloids. The proposed solution harnesses industrial waste - currently relegated to landfills - as a resource, aligning with sustainable practices and environmental responsibility.

Magnesium potassium phosphate cement (MKPC), a type of chemically bonded phosphate ceramic (CBPC), presents a promising alternative to ordinary Portland cement (OPC). This study focuses on developing sustainable MKPC (sust-MKPC) as a thermally passive material for building applications. A low-grade magnesium oxide (LG-MgO) industrial by-product was utilized to formulate sust-MKPC, with hydrogen peroxide employed as an air-entraining agent (AEA) to induce high porosity and enhance thermal insulation while supporting sustainability goals by reducing energy consumption in climate control systems. Seven formulations incorporating varying hydrogen peroxide contents (0, 1, 2, 3, 5, 7.5, and 10 wt.%) were prepared to evaluate the impact of AEA on the thermal and physicomechanical properties. Comprehensive characterization, including porosity and thermal conductivity measurements, revealed that increasing the AEA content significantly improved thermal inertia and lowered thermal conductivity due to porosity. However, this enhancement was accompanied by a marked reduction in mechanical strength and density, highlighting the trade-off between thermal performance and structural integrity in porous sust-MKPC formulations.

Currently, the cement industry stands as one of the sectors with the most significant environmental impact, primarily due to its substantial greenhouse gas emissions and energy consumption. To mitigate this impact, a roadmap has been followed in recent years, outlining a set of objectives aimed at diminishing the environmental footprint of the construction industry. This research focuses on the development of mortars with different water/cement ratios employing an alternative cement, specifically magnesium phosphate cement (MPC) formulated with secondary sources. The goal of this research relays in developing mortars based on MPC by using waste from the metallurgical industry, named tundish deskulling waste (TUN), as an MgO source. The results revealed the optimal water/cement (W/C) ratio for MPC-TUN mortars production through the assessment of various characterization techniques, which was 0.55. This ratio resulted in the highest compressive strength after 28 days of curing and the formation of a stable K-struvite matrix. Furthermore, it demonstrated the effectiveness of aluminum sulphate in preventing efflorescence caused by carbonates. The development of alternative masonry mortars for application in building materials represents a significant stride towards advancing the principles of a circular economy, in alignment with the objectives laid out in the 2030 roadmap.